Organic thin film electroluminescene devices were fabricated using by molecularly doped method with N,N`-diphenyl-N,N`-bis(3-methylphenyl)-1,1`-biphenyl-4,4`-diamine(TPD) as a hole transport material, tris(8-quinolinolate) aluminium(III)(Alq3) as an emitting and electron transport agent, fluorescent squarylium(SQ) dye as a dopant, and poly(methylmethacrylate) as polymer materials. A cell structure of ITO/TPD-PMMA/Alq3-dopant/Mg was employed. The EL spectrum covers a wide range of the visible region and orange emission os observed. Two peaks at 520 and 660nm correspond to the emissions 620nm Alq3 and SQ dye, respectively.

Liquid crystal-polymer composite(LCPC) films are promising new materials for both projection displays and vision products. LCPC films consist of a continuous liquid crystal phase embedded in a three- dimensional network of polymer matrix. The liquid crystal in these LC phases can be electrically switched giving rise to an opaque scattering off-state and a transparent, non- scattering on-state. In this work, a premixture is composed of LC, UV-curable monomer and photonitiator. LCPC films are formed by photopolymerization induced phase separation from this premixture. In conclusion, structure and electro-optical properties of LCPC films strongly depends on the selection of monomer, LC content and curing rate.

1, 4-Diketo-3, 6-diphenyl-pyrrolo-[3, 4c]-pyrrole(abbriviated DPP) is a new heterocyclic pigment of red color whose chlorinated derivative is now on the market. DDP was synthesized from benzonitrile and diethylsuccinate. Pariser-parr-pople(PPP) molecular orbital calculations have been carried out on the DPP in other to study spectroscopically the DPP chromophore on deprotonation.

Photosensitive resin of azide type is good for resolution and inner solvent, but it is really problem to development of practical use because fanctional groups of polymer has many hydrophilic radicals. By careful attention to this point, this study was investigated synthesis term, photo property and development property of composed photosensitive resin of azida type, it is to this effect. 1) H-NMR spectrum of compared DABCI showed amion redical by 6.0~6.1ppm to substitude for azide radical by amino radical by 8.9~9.45ppm, and FT-IR absorption spectra showed the absorption bends at 2100cm. 2)FT-IR absorption spectra of PHS1-DAB, PHS2-DAB, CMM-DAB and CHM-DAB showed azida radical pick to be lost at after irradiation by UV light. 3) According to exposuer change of PHS1-DAB, PHS2-DAB, CMM-DAB and CHM-DAB, absorption maximum value of UV spectrum change was 280nm. 4) to compared relative sensitivity of compared photosensitive resin, PHS2-DAB was the best and to compared insolubility rate of compared photosensitive resin, CMM-DAB was the lower. 5)Solubility if NaOH was the best by 1.0mol/ and solubility of developing solution of ethanol to water was it in the ratio of 4 to 1.