Earticle

Cellulose nanocrystals (CNCs) extractable from plants have excellent biodegradability and biocompatibility. Also, the CNC films can be easily fabricated via solution process. In this respect, the CNCs are emerging materials for various applications. For a use of CNCs in electronic devices, mixing CNCs with other functional nanomaterials can be an efficient strategy to increase conductivity. In this study, we fabricated and characterized CNC-graphene hybrid films on a polyethylene terephthalate substrate using a bar-coating method. The changes in the sheet resistance of the flexible CNC films were observed by varying the graphene dispersion ratio. The structural property and electronic structure of CNC-graphene films were investigated using scanning electron microscopy and X-ray photoelectron spectroscopy. Based on these results, we discuss the physical origin of changes in the sheet resistance. In addition, we fabricated the CNC-graphene paper by adding a glycerol additive. The properties of the CNC-graphene paper were significantly varied by the choice of a graphene dispersion type. The use of graphene dispersion including functional groups results in higher uniformity. Thus, the same sheet resistance values of CNC-graphene paper could be obtained on both front and back sides.

본 연구에서는 Solution Process를 적용한 Strontium Oxide를 배향막으로 사용한 경우의 액정배향 특성에 대해서 연구하였다. Stronium Oxide 는 High K 물질로 배향막으로 사용할 경우 임계치 전압을 효율적으로 조절할 수 있는 장점이 있으나, 액정분자와의 배향에 관한 상호관계에 대해서는 많은 연구가 진행되지 않았었다. 0.1～0.4 Mol 롤 농도를 조절한 Strontium Oxide를 Solution Process 로 배향막으로서 제조함으로써, 보다 생산성이 좋은 방법을 제시할 수 있었으며, 재료가 갖는 우수한 특성을 반영한 액정디 스플레이의 제조가 가능하였다. 샘플 측정결과 1.447～1.613V 의 임계치 전압특성을 보여주어 기존의 방법으로 제조된 액정디스플레 이와 동등 혹은 우월한 특성을 갖고 있음을 알 수 있었다.

We stuidied liauid crystal alignment treatment using solution process for making thin oxide layer in liquid crystal display. It is the one of very effient and popular process in making thin oxide layer in electronical industrial fields. Particularly, this process has highly potential value in liquid crystal display industrial fields because it cause automatically induced alignment process without tranditional alignment process in liquid crystal alignment process. We made several different kinds of mol density solutions using strontium oxide solution. And those solutions were treated for solidification layers using annealing process for 2 hours. And we stuided pretilt angle properties of these alignment layers of strontium oxide for clarifying the relationship of liquid crystal molecules and thin strontium oxide layer. And we also tested the existence of strontium oxide thin layer on substrate using XPS measurement. We expected the hig gain of electro-optical properties in liquid crystal display using strontium oxide thin layer because it has high K property material than the other metal-based oxide layers. In this results, we measured 1.447 to 1.613 thresholds volts as 0.1 mol to 0.4 mol density in 0.1 mol density steps. This is significant better characteristics than conventional liquid crystal display as higher than 1.85 thresholds volts. And it make possible to making next-generation liquid crystal display which present low-power consumption and wide gray scale in liquid crystal display.

This study investigated the electrochemical recovery of palladi ed for palladium leaching. Thehigh acidity of HCl solution and the low concentration of Pd ions increased the cathodic overpotential and reduced the limitingcurrent density. Lowering the current density produced dense deposits; however, they were under high tensile stress. Raising thetemperature affected both the densification and the stress, which enabled the attainment of dense Pd deposits under low stress.Lowering the current density and raising the temperature up to 70oC was recommended for the recovery of palladium as soundbulk Pd deposits. Current efficiency was over 85% at the initial stage of recovery and gradually decreased with the passage oftime. The reduction of the Pd ion concentration during the batch-type recovery may decrease the current efficiency, since a lowPd ion concentration results in a low limiting current density.

In this work, the yttrium oxide(Y2O3) thin films as the buffer layer were prepared by the simple solution coating and reel-to-reel process on an unpolished metal tape substrate. The Y2O3 thin films were successfully synthesized by the hydrolysis of yttrium acetate. We have studied the improvement of surface roughness with the concentration of solution(0.1 M, 0.4 M, M) and the number of coatings. The planarization by solution coating process is simple in comparison with the existing polishing process, and it is eco-friendly, and has the benefits of low cost process. The thickness of Y2O3 films was increased with the Y2O3 concentration in the solution, and the surface became smoother with the number of coating cycles. Using this process, we have achieved 1.2 nm RMS roughness from a starting roughness of over 31 nm on 25 μm2 area.

제조업에 있어 공정의 효율성은 제품의 경쟁력과 직결되는 중요한 요소이다. 특히 최근 여러 국가와 FTA체결로 인해 국내외 제조업이 치열한 경쟁에 직면함에 따라 생산시간을 보다 단축하기 위한 정교한 작업관리 시스템이 요구되고 있다. 본 연구에서는 동작분석 솔루션을 활용하여 제조공정의 효율성을 제고하는 방안을 모색하고자 한다. 동작분석 솔루션을 활용하여 최적화 검증 후 제조공정을 개선할 경우 추가적인 공정 수정 또는 보완에 소요되는 비용을 절감할 수 있으며, 기업의 생산성 향상이라는 실질적 효과를 도출할 수 있다. 본 연구를 통해 작업현장의 낭비개선, 작업편성효율개선, 기종교체시간 단축, 표준시간 측정 및 작업시스템 표준화 등을 구현할 수 있다.

Efficiency of Process in manufacturing industry is a critical factor to connect directly to competitiveness of product. In particular, due to FTAs with various worlds around the world, the domestic and overseas manufacturing industries are facing intense competitions, and it requires elaborate task management system for shortening production time. This study aims at seeking how to raise efficiency of manufacturing process, using motion analysis solution. When improving the process of manufacturing after verifying optimization using motion analysis solution, it can save costs for additional process, modification, or supplement. It can also deduce practical effect to improve productivity of companies. It is expected that the study will contribute to improve wastes in the work field and task assignment efficiency, to shorten time replacing equipment, to measure standard time, and to standardize task system.

In this study, liquid with carbonized artemisia was developed for the first time that can be used as food additives and outside medicinal agents by burning artemisia species such as Artemisia dubia wall, Artemisia capillaris Thunb, Artemisia montana (Nakai) Pamp), Artemisia keiskeana Miq, Leonurus Japonicus Houtt. etc. In addition, edibility of recovered liquid with carbonized artemisia was verified by comparing the contents according to each ingredient with common refined pyroligneous liquid through the analysis of 9 kinds of organic acid by the species of artemisia, methanol and ethanol. Besides, the result of antimicrobial activities on six kinds of food spoilage and food poisoning bacteria observed by paper disc method for liquid with carbonized artemisia indicated that those two liquids showed strong antimicrobial. At the concentration of 1.5 mg/disc, clear zone for S. sonnei and S. aureus, L. monocytogenes was 13~16 mm, and they showed stronger antimicrobial activities than other strain.

이 연구는 장애인거주시설의 지적장애인 인권침해사건 해결과정에서의 딜레마를 탐색할 목적으로 수행되었다. 이를 위해 질적 사례연구방법을 활용하여 한 장애인거주시설에서 발생한 인권침해사건을 중심으로 그 사건 발생 및 대처 과정에서 나타난 딜레마를 다각도에서 규명하였다. 연구결과, 이용자 차원에서는 지적장애의 특성에 따른 자기진술능력, 자기행위 책임성과 관련된 딜레마가 도출되었다. 직원 차원에서는 정당방어의 범위, 이용자 폭력의 대처방안 부재, 동료고발에 대한 갈등과 관련된 딜레마가 도출되었다. 기관 차원에서는 이용자 대 직원 권리보장, 개인적 돌봄 대 공동생활의 특성이 딜레마로 도출되었다. 이 연구는 비록 한 기관에서 발생한 하나의 인권침해사건과 관련된 딜레마를 규명한 탐색적 연구로서의 한계를 갖는다 할지라도, 그 해결과정에서 한 기관 안에서 나타날 수 있는 다양한 인권관련딜레마를 심층적으로 논의하고 있는 점에서 실천적 함의가 크다.

This study was aimed to explore deeply the ethical dilemmas of staffs in a residential facility for people with intellectual dilemmas. The methodology of qualitative case study was used to closely examine an incident of human rights infringement which occurred in a residential facility for people with intellectual disabilities. By this method, the contexts surrounding the occurrence of the incident and the afterward process of the case settlement were investigated. In regards to people with intellectual disabilities, the dilemma about the competency and credibility of handicapped person’s testimony and the limits of responsibility for his/her own behavior was extracted. In regards to staff, the dilemma about allowable limits of self-defense, absence of standard protocol for handling client’s use of violence, and conflicts surrounding whistle blowing was extracted. In regards to the institution, the dilemma about the confused priority of client’s versus staff’s rights, individual caring versus communal living, extension of self-determination versus compliance with community value was extracted. This study is an explorative study of a single case of human-rights infringement. Despite this limitation, it identified various dilemmas which could occur in the actual field by experience of the staff in a residential facility for people with disabilities and provided foundational data needed for further discussions in the field and in study.

1990년대 이후 정보통신산업의 급속한 발전으로 반도체 및 LCD의 수요가 지속적으로 증가하고 있다. 이에 따라 미세회로 패턴형성에 핵심이 되는 감광제와 이의 희석·제거에 사용되는 고가의 시너, 박리액의 수요가 급격히 증가하고 있어, 폐시너, 폐박리액에 대한 재활용 필요성이 대두되고 있는 실정이다. 최근 경제적인 측면과 환경적인 측면, 효율성에 관한 측면에서 스트리핑 공정폐액의 재활용 기술이 폭넓게 연구되고 있다. 본 연구에서는 스트리핑 공정폐액의 재활용 기술에 대한 특허와 논문을 분석하였다. 분석범위는 1981년~2010년까지의 미국, 유럽연합, 일본, 한국의 등록/공개된 특허와 SCI 논문으로 제한하였다. 특허와 논문은 키워드를 사용하여 수집하였고, 기술의 정의에 의해 필터링 하였다. 특허와 논문의 동향은 연도, 국가, 기업, 기술에 따라 분석하여 나타내 보았다.

Since the 1990s, the rapid development of information and communication industry, the demand for semiconductor and LCD continues to increase. Therefore in the formation of fine circuit patterns, which are the cores of sensitizer and the most expensive thinner and stripper liquor used to remove photoresist and its dilution, the amount in demand are dramatically increasing, emerging need for recycling of waste thinner and stripper liquor. Recently, recycling technologies of stripping process waste solution has been widely studied by economic aspects and environmental aspects, in terms of efficiency of the stripping process. In this study, analyzed paper and patent for recycling technologies of waste solution from stripping process. The range of search was limited in the open patents of USA (US), European Union (EP), Japan (JP), Korea (KR) and SCI journals from 1981 to 2010. Patents and journals were collected using key-words searching and filtered by filtering criteria. The trends of the patents and journals was analyzed by the years, countries, companies, and technologies.

본 연구에서는 새도우마스크 제조공정 중 발생되는 Fe-Ni 계 폐산용액을 효율적으로 재활용하기 위하여 폐산용액을 자체 제작한 분무열분해 system을 이용하여 분무열분해시킴에 의해 평균입도 100 nm 이하의 니켈 페라이트(NiFe2O4) 나노 분말을 제조하였으며 반응온도, 용액의 농도 및 용액 유입속도의 반응인자들의 변화에 따른 생성된 분말의 특성변화를 파악하였다. 반응온도가 800~1100oC로 증가함에 따라 분무열분해 공정에 의해 생성된 분말의 평균입도가 현저히 증가하였고 점점 치밀한 조직을 나타내었으며 비표면적은 크게 감소하였다. 반응온도의 증가에 따라 니켈 페라이트 상의 생성비율 및 결정성이 증가하였다. 원료용액의 농도가 증가됨에 따라 분말의 평균입도는 점점 증가하고 비표면적은 감소하는 반면 입도분포는 더욱 불규칙하게 나타났다. 용액의 농도 증가에 따라 니켈 페라이트 상의 생성비율 및 결정성은 현저히 증가하고 있었다. 용액의 유입속도 증가에 따라 분말들의 평균입도는 현저히 증가하고 비표면적은 감소하는 반면 입도분포는 불규칙하게 되며 조직의 치밀성도 감소하였다. 용액의 유입속도 감소에 따라 니켈 페라이트 상의 결정성 및 생성비율이 현저히 증가하고 있었다.

In order to efficiently recycle the waste solution resulting from shadow mask processing, nano-sized Ni-ferrite powder was fabricated through spray pyrolysis process. The average particle size of the powder was below 100nm. In this study, the effects of the reaction temperature, the concentration of raw material solution and the injection speed of solution on the properties of powder were respectively investigated. As the reaction temperature increased from 800oC to 1100oC, average particle size of the powder significantly increased and powder structure became more solid, whereas its specific surface area was greatly reduced. Formation rate and crystallization of NiFe2O4 phase increased along with the temperature rise. As the concentrations of iron and nickel components in waste solution increased, particle size of the powder became larger, particle size distribution became more irregular, and specific surface area was reduced. Formation rate and crystallization of NiFe2O4 phase increased significantly along with the increase of the concentration of solution. As the inlet speed of solution increased, particle size of the powder became larger, particle size distribution became wider, specific surface area was reduced and powder structure became less solid. As the inlet speed of solution decreased, formation rate and crystallization of NiFe2O4 phase significantly increased.

실리콘 웨이퍼 제조공정 중 발생되는 초산, 질산 및 불산을 함유한 3성분계 폐혼산으로부터 개별산으로 분리하여 재활용할 목적으로 용매추출법을 적용하였다. 각 산의 분리를 위해 사용한 추출제로는 초산의 경우는 EHA(2-Ethylhexlalcohol)를 사용하였고, 질산과 불산의 경우에는 TBP(Tri-butlyphosphate)를 사용하여 각 산의 분리과정에 대한 공정설계를 위한 기초 data를 얻고자 하였다. 3성분계 페혼산에서 초산을 추출·분리하고 이후 추출여액 중 질산 및 불산을 순차적으로 추출·분리 할 수 있는 연속공정개발을 위하여 기초 실험 자료와 McCabe-Thiele해석을 통해 최적 투입유량비(O/A), 소요단수(Stage) 등을 결정하였다. 분석 결과 혼산으로부터 초산의 회수율은 90%이상 이었으며 초산 추출여액에서 질산의 회수율은 90%, 최종 추출잔류액에서 불산의 회수율은 67%이상 이었다.

Recovery of acids from the waste etching solution of containing acetic, nitric and hydrofluoric acid discharged from silicon wafer manufacturing process has been attempted by using solvent extraction method. EHA(2-Ethylhexlalcohol) for acetic acid and TBP(Tri-butly Phosphate) for nitric and hydrofluoric acid as a extraction agent was used to the experiment to obtain the process design data in separation procedure.From the experimental data and McCabe-Thiele diagram analysis, we obtained the optimum conditions of phase ratio(O/A) and stages to separate each acid sequently from the mixed acids. The recovery yield was obtained above 90% for acetic acid from the acid mixtures, 90% for nitric acid from acetic acid extraction raffinate and then above 67% for hydrofluoric acid from final extraction raffinate.

본 연구에서는 바나듐광 염배소-수침출 과정을 거쳐 얻어지는 바나듐 함유 수용액으로부터 바나듐을 암모늄메타바나데이트로 침전시켜 회수할 때, 수용액에 존재하는 다른 성분의 이온들이 바나듐 회수에 미치는 영향을 알아보았다. 바나듐 함유 수용액은 pH가 13 정도인 강알칼리 용액으로서, 암모늄메타바나데이트 침전효율을 높이기 위해서는 수용액 pH를 9 이하로 낮춰야 한다. 그러나 황산으로 수용액 pH를 조절하는 과정에서 알루미늄 이온은 바나듐과 같이 공침되기 때문에 알루미늄 이온을 먼저 제거시켜야 한다. 본 연구에서는 소듐실리케이트를 사용하여 알루미늄-실리케이트 화합물 형태로 침전시킴으로서 알루미늄을 제거하였으며, 이 과정에서 바나듐 손실을 최소화하는 조건에 대하여 알아보았다. 알루미늄 제거 후, 황산을 이용하여 수용액 pH를 9 이하로 조절하는 과정에서 수용액의 실리케이트성분을 침전시켜 제거하였다. 이 때 황산의 농도와 첨가속도가 바나듐 손실에 큰 영향을 미치며, 가급적 25% 묽은 황산을 사용하여 천천히 첨가함으로서 바나듐 손실을 최소화 하였다. 알루미늄 제거 그리고 수용액 pH 조절 과정을 통하여 얻은 바나듐 수용액에 3 당량의 염화암모늄을 첨가하여 상온에서 침전시킨 결과, 전체적으로 81% 이상의 바나듐을 암모늄메타바나데이트로 회수할 수 있었다. 회수된 암모늄메타바나데이트를 세척한 후 550℃에서 2시간 열처리하여 98.6% 순도의 오산화바나듐을 얻을 수 있었다.

In this study, the effects of solution components were investigated in the recovery of vanadium as ammonium metavanadate from vanadium-ore-salt roasting?water leaching solution. The vanadium-containing solution is strongly alkaline (pH 13), so the pH must be lowered to 9 or less to increase the ammonium metavanadate precipitation efficiency. However, in the process of adjusting the solution pH using sulfuric acid, aluminum ions are co-precipitated, which must be removed first. In this study, aluminum was precipitated in the form of an aluminum-silicate compound using sodium silicate, and the conditions for minimizing vanadium loss in this process were investigated. After aluminum removal, the silicate was precipitated and removed by adjusting the solution pH to 9 or less using sulfuric acid. In this process, the concentration and addition rate of sulfuric acid have a significant influence on the loss of vanadium, and vanadium loss was minimized as much as possible by slowly adding dilute sulfuric acid. Ammonium metavanadate was precipitated using three equivalents of ammonium chloride at room temperature from the aluminum-free, aqueous solution of vanadium following the pH adjustment process. The recovery yield of vanadium in the form of ammonium metavanadate exceeded 81%. After washing the product, vanadium pentoxide with 98.6% purity was obtained following heat treatment at 550 ℃ for 2 hours.

FeCl 3 용액은 금속의 에칭용액으로 사용되며, 사용 후 발생하는 FeCl 3 에칭폐액은 환경적, 경제적으로 문제를 지니기 때문에 에칭액을 재사용할 필요가 있다. 본 연구에서는 FeCl 2 용액에 HCl을 첨가 한 후, 산화제로 H 2 O 2 를 첨가하여 용액 내 Fe 2+ 를 산화시켰으며, 산화과정에서 산화-환원전위(ORP)와 산화율 간의 관계를 조사하였다. ORP는 HCl과 H 2 O 2 의 농도가 증가함에 따라 증가하였으며, 산화가 진행되면서 점차 감소하여 Nernst 식과 일치하는 결과를 보였다. 또한 충분한 양의 HCl과 H 2 O 2 를 첨가하였을 경우, 약 99% 이상 산화가 이루어짐을 알 수 있었다.

The FeCl 3 solution has been used as an etchant for etching of metal. It is necessary to reuse the etching solution because waste FeCl 3 etchant generated after use has provided environmental and economic problems. In this study, HCl was mixed with the FeCl 2 solution and then H 2 O 2 was added into the mixed solution to oxidize the Fe 2+ . During the oxidation process, oxidationreduction potential (ORP) was measured and the relationship between ORP and oxidation ratio was investigated. As a result, this study found that the ORP was increased with increasing the concentration of HCl and H 2 O 2 , while the ORP is decreased with oxidation progress. Such a behavior was in good agreement with Nernst’s equation. Also, the oxidation efficiency reached about 99% when a sufficient amount of HCl and H 2 O 2 were added.

추출제로 Cyanex 572를 사용하여 염산용액에서 [Sm]과 [Pr, Nd]그룹을 분리하기 위해 Xu Guangxian이 제시한 이론에 의하여최적 향류 추출 공정 변수를 계산하고자 하였다. 기초실험으로부터, [Sm]/[Pr, Nd]의 두 그룹 최적 분리계수는 추출공정의 경우 pH 1.75에서 14.59, 세정공정에서는 0.01M HCl에서 14.61 이었다. [Sm]과 [Pr, Nd] 그룹분리에 필요한 공정 변수에 대해 계산을 하였다. 계산 결과 두 그룹의 희토류 분리에 필요한 총 추출 및 세정 단수는 11단이었으며, 최적추출비를 유지시키기 위해 필요한 원료용액, 추출용액 및 세정용액의 유량비는 0.1 M HCl을 사용하였을 경우 6.25 : 1.74 : 5.80 이었다.

For the purpose of optimizing the counter current extraction process for separation of [Sm] and [Pr, Nd] group in hydrochloric acid solution using Cyanex 572 as an extractant, the theory of Xu Guangxian was derived for calculating the optimized extraction factors. From the basic batch test result, the separation factor of [Sm]/[Pr, Nd] was 14.59 at pH 1.75 in extraction process and 14.61 at 0.01 M HCl in scrubbing process. The process parameters can be calculated using a theory of optimum extraction ratio. From the result of calculation, the total extraction and scrubbing stage numbers at counter current process were 11 and for maintain extraction ratio the flow rate ratio of feed solution, solvent solution, scrubbing solution was 6.25 : 1.74 : 5.80 using 0.1 M HCl.

폐리튬이온전지를 용융환원시키면 구리, 코발트, 철, 망간, 니켈 및 규소를 함유한 금속합금을 얻는다. 금속합금의 황산침출용액에서상기 금속을 분리하기 위한 공정을 개발하여 발표하였다. 이 공정에서는 철(III)과 구리(II)를 분리하기 위해 이온성액체를 사용하였다. 본연구에서는 이온성액체를 대체하기 위해 D2EHPA와 Cyanex 301을 추출제로 사용했다. 철(III)과 구리(II)는 황산침출액으로부터 0.5 M 의 D2EHPA에 의한 3단의 교차추출 및 0.3 M의 Cyanex 301로 분리하는 것이 가능했다. 유기상으로부터 철(III)과 구리(II)의 탈거는 각각 50%와 60%의 왕수로 가능했다. 연속실험의 물질수지로부터 금속의 회수율과 순도는 99%이상으로 확인되었다.

The smelting reduction of spent lithium-ion batteries results in metallic alloys containing Co, Cu, Fe, Mn, Ni, and Si. A process to separate metal ions from the sulfuric acid leaching solution of these metallic alloys has been reported. In this process, ionic liquids are employed to separate Fe(III) and Cu(II). In this study, D2EHPA and Cyanex 301 were employed to replace these ionic liquids. Fe(III) and Cu(II) from the sulfate solution were sequentially extracted using 0.5 M D2EHPA with three stages of cross-current and 0.3 M Cyanex 301. The stripping of Fe(III) and Cu(II) from the loaded phases was performed using 50% (v/v) and 60% (v/v) aqua regia solutions, respectively. The mass balance results from this process indicated that the recovery and purity percentages of the metals were greater than 99%.

망간단괴 매트상 침출액 조성으로 제조 된 모의 용액(Cu 10.5 g/L, Co 2.0 g/L, Ni 15.0 g/L, Fe 0.2 g/L)으로부터 용매추출- 전해채취 연속공정을 통해 구리를 분리-회수하기 위하여 규모 확대용 용매추출장치인 6단 혼합-침강기(mixer-settler : 추출 4단, 탈거2단)와 전해조를 이용하였다. 용매추출의 경우 추출제로는 40%(v/v)의 LIX 84I, 탈거용액은 전해폐액(Cu 35.0 g/L, H2SO4 180 g/L)을사용하였으며 추출단과 탈거단의 O/A 비는 각각 1/1과 1.5/1 이었다. 용매추출공정의 구리의 추출율과 탈거율은 각각 96.7%와 91.0%이었으며 탈거액(전해액)의 구리, 니켈, 코발트 그리고 철의 농도는 각각 50~51 g/L, 25 ppm, 5 ppm 그리고 3 ppm 이었다. 전해채취공정은 1.50 A/dm2 의 전류밀도에서 98.9%의 전류효율을 나타내었으며, 99.833% 순도의 금속 구리를 얻었다.

A scale-up test with a continuous solvent extraction and electro-winning system was carried out to separate and recover copper from a synthetic sulfuric acid solution (Cu 10.5 g/L, Co 2.0 g/L, Ni 15.0 g/L, Fe 0.2 g/L). The solution was introduced into mixer-settlers with four stages of extraction and two stages of stripping for continuous countercurrent solvent extraction to separate copper from nickel and cobalt. The loading was carried out using 40% LIX 84-I(v/v) as extractant with a phase ratio of A : O = 1 : 1. Meanwhile, the stripping was undertaken at a phase ratio of A : O = 1 : 1.5 using depleted electrolyte containing 35.0 g/L Cu and 180 g/L H2SO4 as stripping solution. The extraction and stripping efficiencies were found to be 96.7% and 91.0%, respectively. The copper composition of the stripped solution (pregnant electrolyte) was 50.0 g/L Cu with impurities of 25 ppm nickel, 5 ppm cobalt and 3 ppm iron. In the electro-winning process, copper metal of 99.833 purity was yielded with current efficiency of 98.9% and current density of 1.50 A/dm2 .

본 연구에서는 새도우마스크 제조공정 중 발생되는 Fe-Ni계 복합 폐산을 원료로 하여 공기압력 1 kg/cm2의 조건에서 분무열분해 공정에 의해 평균입도 100 nm 이하의 니켈 페라이트(NiFe2O4) 및 Fe2O3+NiO 나노 분말을 제조하였으며, 반응온도, 폐산 용액의 농도 및 nozzle tip 크기의 반응인자들의 변화에 따른 생성된 분말의 특성 변화를 파악하였다. 반응온도가 800oC로부터 1100oC로 변화함에 따라 분말의 평균입도는 40 nm로부터 100 nm 정도까지 증가하고 있었으며 조직은 더욱 치밀화되는 반면 입도분포는 점점 불균일하게 됨을 알 수 있었다. 반응온도의 증가에 따라 니켈 페라이트 상의 생성 비율이 현저히 증가하고 있었으며, 분말의 비표면적은 현저히 감소하고 있었다. 원료용액 내의 Fe 성분의 농도가 20 g/l로부터 200 g/l로 증가됨에 따라 분말의 평균 입도는 30 nm로부터 60 nm 정도까지 점점 증가하는 반면 입도분포는 더욱 불균일하게 나타나고 있었다. 또한 용액의 농도 증가에 따라 니켈 페라이트 상의 생성 비율이 증가하고 있었으며, 분말의 비표면적은 현저히 감소하였다. Nozzle tip 크기 증가에 따라 분말의 입도분포는 점점 불균일하게 나타나는 반면 평균 입도는 현저한 변화를 나타내지 않았다. Tip 크기가 2 mm까지는 tip 크기 증가에 따라 니켈 페라이트 상의 생성 비율에 현저한 변화는 나타나지 않는 반면 분말의 비표면적은 약간 감소하였다. Tip 크기가 3 mm 및 5 mm로 증가하는 경우에는 니켈 페라이트 상의 생성 비율이 점점 감소하고 있었으며, 분말의 비표면적은 약간씩 증가하고 있음을 알 수 있었다.

In this study, nano-sized Ni-ferrite and Fe2O3 condition of 1kg/cm2air pressure using the Fe-Ni complex waste acid solution generated during the manufacturing process of shadow mask. The averageparticle size of the produced powder was below 100 nm. The effects of the reaction temperature, the concentration of raw materialsolution and the nozle tip size on the properties of powder were studied. As the reaction temperature increased from 800oC to1100oC, the average particle size of the powder increased from 40 nm to 10 nm, the structure of the powder gradualy became solid,ction ofthe Ni-ferrite phase were also on the rise, and the surface area of the powder was greatly reduced. As the concentration of Fe in solu-tion increased from 20 g/l to 20 g/l, the average particle size of the powder gradualy increased from 30 nm to 60nm, while the dis-tribution of the particle size apeared more irregular. Along with the increase of the concentration of solution, the fraction of the Ni-ferrite phase was on the rise, and the surface area of the powder was greatly reduced. Along with the increase of the nozzle tip size,t change.As the nozzle tip size increased from 1 m to 2 m, the fraction of the Ni-ferrite phase showed no significant change, while thesurface area of the powder slightly reduced. As the nozzle tip size increased to 3 m and 5 mm, the fraction of the Ni-ferritephase gradually reduced, and the surface area of the powder slightly increased.

본 연구에서는 TiCl4와 IPA의 반응으로 TiO2 나노 용액을 합성한 뒤 글라스 기판에 반복 코팅하여 박막을 제작하고, 코팅 횟수에 따른 광학적·전기적 특성 변화를 분석하였다. 반사도 및 확산 반사 결과, 코팅 횟수 증가에 따른 박막 두께 증가와 광 간섭 효과로 스펙트럼 피크 이동과 반사 특성 변화가 나타났다. PL 분석에서는 코팅 횟수 증가에 따라 발광 강도가 감소하였으며, 이는 결함 밀도 감소와 비복사 재결합 경로 증가에 기인한 것으로 해석된다. 또한 표면저항은 코팅 횟수가 증가할수록 증가하여 절연 특성이 강화됨을 확인하였다. 이러한 결과는 용액 공정 기반 TiO2 박막에서 두께 및 결함 제어를 통해 광·전기적 특성 조절이 가능함을 보여주며, 광전자 소자와 기능성 코팅 응용을 위한 기초 자료를 제공한다.

This study synthesized a TiO2 nano-solution through the reaction between TiCl4 and isopropyl alcohol (IPA) and fabricated TiO2 thin films on glass substrates via repeated coating. The optical and electrical properties were systematically analyzed as a function of coating cycles, revealing that increased film thickness and optical interference caused spectral peak shifts and changes in reflectance behavior. Photoluminescence (PL) analysis showed a decrease in emission intensity with increasing coating cycles due to reduced defect density and enhanced non-radiative recombination pathways. In addition, sheet resistance increased with the number of coatings, confirming enhanced electrical insulating properties. These results demonstrate that the optical and electrical properties of solution-processed TiO2 thin films can be effectively controlled through thickness and defect engineering, providing fundamental insights for optoelectronic devices and functional coating applications.

8·15해방 후 신생 대한민국이 출범한 지 5개월여 지나서, 이승만정부 내 현직 장관의 독직 사 건이 잇달아 발생하였다. 두 달여의 시차를 두고 터진 두 독직 사건은 야당 권력과 정부 권력 사이 의 갈등에서 비롯되었다는 공통점이 있었으나, 임명권자인 대통령 이승만이 양자에 대응하는 방식 은 전혀 달랐다. 수사 주체인 검찰 및 이를 지휘·관할하는 법무부장관이 통치권자의 의중을 반영 하여 사건을 수습하려 했던 이유였다. 임영신 독직 사건은 감찰위원회가 ‘파면’으로 곧장 여론화하자, 당시 언론들이 거의 실시간에 가깝게 보도하였는데도, 조봉암 독직 사건과 달리 기소가 이루어지기 전부터 전혀 다른 해법이 모 색되었다. 이승만은 애초 임영신에게 상공부장관직을 사임하는 선에서 사태를 마무리하자고 권하 였으나, 임영신은 오히려 임명권자를 설득하고 여론에 항변하면서 완강하게 버티다가, 5월 28일 조봉암과 같은 날짜로 불구속 기속되었다. 이 과정에서 이승만은 시종일관 임영신을 엄호하였으 므로, 법무부장관 李仁은 임영신의 기소를 저지하려 노력하면서, 이승만의 의중에 따라 검찰 측과 ‘정치적 해결’을 시도하였다. 이때 ‘정치적 해결’이란 임영신이 독직 의혹들에 책임을 지고 1946년 5월 27일까지 상공부장관직 을 사임하면, 검찰은 그를 기소하지 않고 사건을 마무리짓는다는 타협이었다. 이러한 해법이 법무 부장관 이인 - 검찰총장 권승렬 - 서울지방검찰청 검사장(서울지검장) 최대교 3자 사이에 합의된 상태였다. 이승만정부가 내각을 구성한 지 채 6개월도 되지 않아 연발한 두 독직 사건은 정권의 도덕성에 흠집을 내었을 뿐 아니라, 갓 출발한 대한민국의 정체성에도 타격을 주었다. 더욱이 임영신은 당 시 권력의 제2인자로 불릴 만큼 이승만의 최측근이었으므로, 그의 독직 사건은 始端부터 결말까지 ‘정치적 성격’으로 일관하였다. 이 논문에서 의미하는 ‘정치적 해결’은, 임영신이 상공부장관직을 사임한다면 불기소 처리한다 는 합의점―이인 등이 회고한―보다 더 넓은 범주이다. 임영신 독직 사건이 발단하자, 대통령 이승 만부터 사법 당국인 검찰·법무부가 조봉암 독직 사건과 달리 대응하는 양상을 비롯하여 사법부 의 최종 판결에 이르는 모든 과정에서, 사법의 잣대가 아닌 算術과 방식으로 사건을 마무리하려는 일체의 시도와 행태를 가리켰다.

It was about five months of the liberation of August 15 after the inauguration of the Korean government inaugurated that a series of corruption scandal of incumbent ministers in the Lee Seung-Man Government continually occurred. Lim Young-sin’s corruption was the second one after Agriculture Minister Cho Bong-am’ scandal. The two cases, which broke out over a two-month time difference, had something in common that they stemmed from a conflict between opposition power and administrative power. Lim Young-sin was a heavyweight even within the pro-Lee Seung-Man forces, and the time of the Lim Young-sin graft scandal was in the midst of a power struggle between the leading opposition party and the adminis tration. Since the cor ruption case of the powerful forces had a ‘political character’ that would lead to a crisis in the regime, it was an issue that the pro-Lee Seung-Man group had to end with a ‘political solution’. Initially, Lee Seung-Man intended to recommend Lim Young-sin to end the situation by resigning her the position of Minister of Commerce and Industry. However, Lim Young-sin was indicted without detention on May 28, 1949, after persuading the appointing authority and protesting against public opinion. In this process, Lee Seung-Man tried to cover Lim Young-sin throughout. This was the reason why the prosecution that was the subject of the investigation, and the Minister of Justice, who reflected the intention of the ruler commanding the jurisdiction, tried to settle the case in this way. In particular, Lee Yin, the Minister of Justice tried to block Lim Young-sin’s prosecution, and attempted to have a ‘political solution’ with the prosecution according to Lee Seung-Man’ intention. At this time, the ‘political solution’ was a kind of compromise that if Lim Young-sin would resign as the Minister of Commerce and Industry by May 27, the prosecution could conclude as a case without prosecuting her. The 'political solution’ that this paper means has a broader category than the compromise that Lim Young-sin would not indict if she resigned as the Minister of Commerce and Industry. When the Lim Young-sin’s corruption scandal happened, the response from the aspects of President Lee Seung-Man and the Minister of Prosecution and Justice to the final ruling of the judiciary, pointed out to all actions to end the case with political arithme tic, not judicial standards.

The analytic hierarchy process is known as a useful tool for the group decision making methods. This tool has been area such as investment, R&D management, manufacturing, production and marketing. Typically, transportation problems have addressed by mathematical programming. In this paper, an optimal solution of transportation problem was determined by the analytic hierarchy process.

최근에 유연 전자소자에 대한 다양한 연구가 이루어지고 있다. 본 연구에서 유연 전자소자용 금속기반의 투명 전도 막으로 Ag 나노와이어로 그 가능성을 평가하였다. 이를 위해 신개념의 브러시 코팅법과 상압플라즈마 기반의 아르곤 플라즈 마 증발법으로 Ag 나노 물질을 글라스에 형성시켰다. 먼저 브러시로 Ag 용액을 글라스에 코팅하고, 남아있는 용매는 상압플 라즈마로 제거한다. 이 용매 증발 과정에서 상압플라즈마와 용매의 반응에 의해 소리가 발생하기 때문에 용매의 남아있는 정 도를 확인할 수 있다. 막의 코팅 횟수에 따른 반사도, 투과도, 흡수도와 같은 광특성 및 전기적인 결과들을 관찰하기 위하여 최대 5번 코팅하여 그 결과들을 분석하였다. 광에 의한 Ag 나노와이어와의 상호작용을 조사할 목적으로 빛의 파장을 200nm 부터 800nm까지 변화시키면서 반사도 및 투과도를 측정하였으며, 반사도와 투과도 모두 5번 코팅한 샘플에서 가장 큰 변화 를 나타내었다. 특히 흡수도의 경우 반사도나 투과도의 데이터와는 다르게 코팅에 따라 Ag 나노와이어의 빛에 대한 흡수도 증가 추이를 명확하게 확인할 수 있었다. 전기적인 특성은 4번 이상 코팅했을 때부터 큰 변화가 있었으며, 특히 5번 진행시 k Ω/cm2보다 낮아진 저항값을 보였다. 이러한 광 및 전기적인 결과들을 기반으로, 향후 전자소자에 적용하여 투명 전도막으 로의 가능성을 검증할 계획이다.

Recently, various studies on flexible electronic devices have been performed. In this study, the potential of Ag nanowires was evaluated as a material to replace the ITO transparent conductive film. Ag nanomaterials were formed on the glass by a novel brush coating method and an argon plasma evaporation method based on atmospheric pressure plasma. First, the Ag solution is coated on the glass with a brush, and the remaining solvent is removed with atmospheric plasma. During this process of solvent evaporation, a sound is generated by the reaction between the atmospheric plasma and the solvent. Therefore, the remaining amount of the solvent can be confirmed. In order to observe optical properties and electrical results such as reflectance, transmittance, and absorbance according to the number of coatings of the film, the results were analyzed by coating up to 5 times. For the purpose of investigating the interaction of light with Ag nanowires, reflectance and transmittance were measured while changing the wavelength of light from 200 nm to 800 nm. In the case of absorbance, the trend of increasing light absorption of the Ag nanowires according to the coating was clearly confirmed. The electrical properties showed a great change from the time of coating more than 4 times, and in particular, the resistance value was lower than kΩ/cm2 when the coating was applied 5 times. Based on these optical and electrical results, we plan to verify the possibility of a transparent conductive film by applying it to electronic devices in the future.