초록

영어

This study evaluated layer-by-layer mechanical and optical properties of commercial multi-layered zirconia blocks. Specimens were prepared from the top, middle, and bottom layers of three products, and biaxial flexural strength, Vickers hardness, and light transmittance were measured. The AM and LD groups showed increased flexural strength and decreased light transmittance from top to bottom, whereas the KK group showed smaller layer-dependent variations. Vickers hardness differed significantly among products but not among layer locations. These results demonstrate that mechanical and optical property gradients vary depending on the design of multi-layered zirconia blocks. The findings may provide useful information for selecting zirconia products and positioning restorations within blocks according to clinical requirements. Further compositional and phase analyses are required to clarify the mechanisms underlying these property gradients.

한국어

본 연구는 상용 멀티레이어 지르코니아 블록의 레이어 위치에 따른 기계적·광학적 특성을 비교하여 제품별 물성구배를 평가하고자 하였다. 상용 제품 3종의 상부, 중부 및 하부에서 시편을 제작하고, 이축 굽힘강도, 비커스 경도 및 광투과율을 측정하여 이원분산분석과 Tukey HSD 사후검정을 시행하였다. AM 및 LD군은 상부에서 하부로 갈수록 굽힘 강도가 유의하게 증가하고 광투과율이 유의하게 감소하였다. 반면 KK군은 굽힘강도의 레이어 간 유의한 차이가 없었으며, 광투과율 변화폭도 상대적으로 작았다. 비커스 경도는 제품군 간 유의한 차이를 보였으나 레이어 위치에 따른 차이는 유의하지 않았다. 이상의 결과로 제품 설계에 따라 레이어별 기계적·광학적 물성 구배가 다르게 나타남을 확인하였다. 본 결과는 임상적 요구에 따른 제품 선택과 블록 내 보철물 위치 설정을 위한 기초자료로 활용될 수 있으며, 향후 조성 및 결정상 분석을 통한 물성 구배의 원인 규명이 필요하다.

목차

요약
Abstract
1. 서론
2. 연구방법
2.1 소결 조건
2.2 시험 방법
2.3 통계 분석
3. 결과
3.1 굽힘강도
3.2 경도
3.3 광투과율
4. 고찰
5. 결론
REFERENCES

키워드

저자

• 송재석 [ Jae-seok Song | ㈜메디클러스 기업부설연구소 책임연구원 ] Corresponding Author

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  미래기술융합논문지

• 간기

  격월간

• eISSN

  2951-2468

• 수록기간

  2022~2026

• 등재여부

  KCI 등재후보

• 십진분류

  KDC 530 DDC 620