This study aimed to develop an antibacterial medical skin adhesive based on NBCA/OCA by incorporating iodine, cellulose nanofiber (CNF), and 1,2-hexanediol to improve its antibacterial and mechanical properties. The Curing time was systematically evaluated according to the NBCA/OCA ratio and the contents of iodine and CNF, and antibacterial activity was compared among formulations containing iodine and 1,2-hexanediol individually or in combination. The final formulation consisted of NBCA/OCA at 8:2, 250 ppm iodine, 500 ppm CNF, and 0.5 wt% 1,2-hexanediol. The Curing time, suture strength, and tensile strength were 36 s, 13.9 ± 3.8 N, and 0.215 ± 0.03 MPa, respectively. The formulation showed a 96.8% reduction in Staphylococcus aureus and was classified as Grade 0 in the cytotoxicity test according to ISO 10993-5. These findings demonstrate the feasibility of designing an NBCA/OCA-based medical skin adhesive with balanced antibacterial, mechanical, and curing properties.

한국어

본 연구에서는 NBCA/OCA 기반 의료용 피부접착제의 항균성과 기계적 성능을 향상시키기 위하여 Iodine, cellulose nanofiber(CNF) 및 1,2-hexanediol을 적용하고 최적 조성을 개발하였다. NBCA/OCA 혼합비와 Iodine 및 CNF 함량에 따른 중합시간을 단계적으로 평가하고, Iodine과 1,2-hexanediol의 단독 및 병용에 따른 항균성을 비교하여 최종 조성을 선정하였다. 최종 조성은 NBCA/OCA=8:2, Iodine 250 ppm, CNF 500 ppm 및 1,2-hexanediol 0.5 wt%로 결정하였다. 개발 조성의 중합시간은 36초, 봉합강도는 13.9 ± 3.8 N, 인장강도는 0.215 ± 0.03 MPa로 나타났으며, Staphylococcus aureus에 대한 항균성은 96.8%의 균 감소율을 나타냈다. 또한 ISO 10993-5에 따른 세포독성 시험에서 Grade 0으로 평가되었다. 본 연구는 항균성과 기계적 성능 및 경화 특성을 종합적으로 고려한 NBCA/OCA 기반 의료용 피부접착제의 조성 설계 가능성을 제시하였다.

목차

요약
Abstract
1. 서론
2. 실험 방법
2.1 재료
2.2 경화시간
2.3 성능평가
3. 결과
3.1 경화시간
3.2 성능 평가
4. 고찰
5. 결론
REFERENCES

키워드

저자

• 안형근 [ Hyeong-Geun Ahn | ㈜이노트 대리 ] Corresponding Author
• 박춘호 [ Choon-Ho Park | ㈜이노트 연구소장 ]
• 황현욱 [ Hyun-Wook Hwang | ㈜이노트 대표이사 ]

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  산업과 과학 [Advanced Industrial SCIence]

• 간기

  격월간

• eISSN

  2951-2476

• 수록기간

  2022~2026

• 등재여부

  KCI 등재후보

• 십진분류

  KDC 004 DDC 004