초록

영어

Ceramic nanocomposite materials composed of mixed oxides exhibit markedly different particle characteristics such as crystal structure, size, and morphology depending on the synthesis method employed, which in turn significantly affects their physical and chemical properties. In the present study, aqueous precursor solutions were prepared by dissolving copper and zinc nitrates in distilled water, and a hydrothermal synthesis approach was adopted to fabricate NiO-CuO-ZnO ternary nanocomposites. The products obtained from the hydrothermal reaction were filtered, dried, and subsequently calcined at 500 ℃ for a fixed duration to yield stable crystalline NiO-CuO-ZnO nanocomposites. The crystalline structure and crystallite size of the synthesized materials were analyzed using X-ray diffraction (XRD), while their surface morphology and microstructural features were examined in detail by scanning electron microscopy (SEM).

한국어

복합 산화물로 구성된 세라믹스 나노복합재료는 합성 과정에서 적용되는 방법론에 따라 형성되는 입자의 결정구조, 크기, 형태학적 특성 등이 크게 달라지며, 이로 인해 물리적·화학적 성질 역시 현저한 차이를 나타낸다. 본 연구에서는 니켈, 구리 및 아연의 질산염을 증류수에 용해하여 수용액 전구체를 제조하였으며, 이를 이용해 수열합성법(hydrothermal synthesis)을 적용함으로써 NiO-CuO-ZnO 삼원 나노복합체를 합성하였다. 수열 반응을 통해 형성된 전구체는 여과 및 건조 과정을 거쳐 500℃의 온도에서 일정 시간 하소(calcination) 처리함으로써 안정한 결정상을 갖는 NiO-CuO-ZnO 나노복합체를 최종적으로 얻을 수 있었다. 합성된 시료의 결정 구조 및 결정립 크기는 X선회절분석(XRD)을 통해 확인하였으며, 표면 형상과 입자의 미세구조는 주사전자현미경(SEM)을 사용하여 정밀하게 관찰하였다.

키워드

저자

• 김수종 [ Soo-Jong Kim ]

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  The Journal of the Convergence on Culture Technology (JCCT) [문화기술의 융합]

• 간기

  격월간

• pISSN

  2384-0358

• eISSN

  2384-0366

• 수록기간

  2015~2026

• 등재여부

  KCI 등재

• 십진분류

  KDC 600 DDC 700