This study analyzed the chemical and mineralogical characteristics of Ridge-end tiles of the Goryeo Dynasty, excavated in Chungcheongnam-do region (Buyeo, Boryeong, and Hongseong) to examine the regional correlations and the characteristics of the production method and also compared and examined the characteristics of ridge-end tiles of Baekje Dynasty in the Sabi Period and the Goryeo Dynasty found in Chuncheongnam-do and those of the Unified Silla Dynasty found in Gyeongju in terms of the materials used by referring to the analysis data from previous studies. As a result, ridge-end tiles of the Goryeo Dynasty of Chungcheongnam-do region excluding ridge-end tiles of the Geumgangsa Temple site in Buyeo were not divided by excavation site by the composition of the clay in terms of chemical properties, but all samples showed similar trends with respect to miscellaneous components and rare-earth elements regardless of the regions. In terms of mineralogical characteristics, ridge-end tiles of the Geumgangsa Temple site is deemed to have undergone relatively high sintering temperature than other samples of similar mineral composition, and other samples did not show correlation as a variety of minerals were found from them. The chemical and mineralogical characteristics of most finals of the Baekje Dynasty in the Sabi Period are not divided by excavation site and thereby showing less correlation by remains, and they showed similar rare-earth element distribution patterns as earlier ridge-end tiles of the Goryeo Dynasty. In other words, it is highly probable that ridge-end tiles of Baekje Dynasty in the Sabi Period and the Goryeo Dynasty found in Chuncheongnam-do collected the raw materials for the clay in a fixed area when they were produced, but it is deemed that there must have been more or less differences in the process of collecting the clay from layers with different degree of aeration for each final and that they must have undergone various sintering temperatures during production. For ridge-end tiles of the Unified Silla Dynasty found in Gyeongju, relatively all samples were divided by remains in terms of chemical characteristics. It is therefore deemed that ridge-end tiles were produced by using different clays and in different production methods. In addition, it is deemed that they were produced at a lower temperature than ridge-end tiles of Chungcheongnam-do as minerals indicating relatively low sintering temperature were found compared with ridge-end tiles from the Sabi Era of the Baekje Dynasty period and the Goryeo Dynasty period regarding the mineralogical characteristics and the actual thermal analysis (TG-DSC) indicated that the sintering temperature they underwent was around 573∼870℃.

한국어

본 연구에서는 충남지역(부여, 보령, 홍성) 고려시대 치미의 화학적, 광물학적 특성을 분석하여 지역별 상관관계와 제작방법의 특성을 살펴보고, 사전에 연구된 분석데이터를 참고하여 충남지역 사비 백제~고려시대 치미와 경주 통일신라시대 치미의 재료학적 특성을 비교 고찰하였다. 그 결과, 화학적 특성에서 부여 금강사지 치미를 제외한 충남지역의 고려시대 치미는 태토 조성에서 출토지별로 구분되지 않지만, 미량성분과 희토류성분은 지역에 상관없이 모든 시료가 비교적 유사한 경향을 나타내었다. 광물학적 특성에서는 금강사지 치미가 유사한 광물조성으로 다른 시료에 비해 비교적 높은 소성온도를 거친 것으로 보이며, 이를 제외한 시료들은 다양한 광물이 검출되어 연관성이 확인되지 않았다. 사비 백제 치미 대부분은 화학적, 광물학적 특성에서 출토지별로 성격이 구분되지 않아 유적별 관련성이 낮은 것을 알 수 있었으며, 앞선 고려시대 치미와 유사한 희토류원소 분포패턴을 나타내었다. 따라서 충남지역 사비 백제~고려시대 치미는 전반적으로 제작 시 일정 지역에서 태토의 원료를 채취하였을 가능성이 높지만, 치미별로 풍화도가 다른 사면에서 태토를 채취하는 과정 등에서는 다소 차이가 있었을 것으로 판단되며, 제작 시 다양한 소성온도를 거쳤을 것으로 추정된다. 경주 통일신라시대 치미는 화학적 특성에서 비교적 모든 시료가 유적별로 구분되었다. 따라서 치미별로 서로 다른 태토를 사용하여 제작하였을 것으로 추정되며, 제작방법 또한 상이하였을 것으로 사료된다. 또한 광물학적 특성에서, 충남지역 치미에 비해 상대적으로 낮은 소성온도를 지시하는 광물이 검출되고, 실제 열분석(TG-DSC)을 통해 573~870℃의 소성온도를 거친 것으로 확인되어 충남지역 사비 백제~고려시대 치미에 비해 낮은 온도에서 제작된 것을 알 수 있었다.

목차

개요
Abstract
I. 서론
1. 연구배경 및 목적
2. 연구대상
II. 분석방법
1. 화학적 특성
2. 광물학적 특성
III. 연구결과
1. 주성분 분석(WD-XRF)
2. 미량원소 및 희토류원소 분석
3. 광물학적 특성
IV. 고찰
1. 충남지역 고려시대 치미의 특성
2. 충남지역과 경주지역 치미의 특성
V. 결론
참고문헌

키워드

충남지역 고려시대 치미 사비백제 경주 통일신라시대 조성성분 Chungcheongnam-do region Goryeo Dynasty Ridge-end tiles sabi baekje Unified Silla in Gyeongju compositions

저자

• 신연홍 [ Shin, Yeon-Hong | 국립부여박물관 ]
• 황현성 [ Hwang, Hyun-Sung | 국립부여박물관 ]
• 이민희 [ Lee, Min-Hee | 국립부여박물관 ]

참고문헌

발행기관

간행물