Analysis on the component of waterproofing paint showed that epoxy primer is the most prone to ignite once blended with hardener, epoxy primer develops the most volatile elements and the lowest flashing point. Most of the paint material tends to have lower flashing point once blended with hardener. Experiments prove that welding sparks can lead to ignition easily and especially so with epoxy primer and epoxy top coat, and urethane primer. Fire transmission speed of these waterproofing materials is much higher than general combustibles. Highest risk of catching fire is right after painting, and as time passes, the flammability decreases. Therefore, there remains flammability even after the painting, thus there should be close monitoring of the site so that there is not welding sparks nearby shortly after painting. Emergency firefighting system should be mandatorily equipped in the site as well. Lastly, protection measures should be implemented publicly. Warning of low flashing points or describing the fire risk with welding sparks on the box of waterproofing material could be one small example.

목차

Abstract
 1. 서론
  1.1 연구 배경
  1.2 연구 목적
 2. 방수도료의 이론적 배경
  2.1 에폭시 바닥재와 우레탄 방수재
  2.2 도장 방법
 3. 화재사례 분석
  3.1 전국 도료화재 발생 현황
  3.2 세종특별자치시 방수도료 화재 사례
  3.3 세종특별자치시 방수도료 화재 분석
 4. 방수도료의 성분분석
  4.1 휘발분과 불휘발분의 함유량 분석
  4.2 주제와 경화제의 혼합 전ㆍ후 인화점 분석
 5. 화재 재연실험
  5.1 미소화원에 의한 착화실험
  5.2 화염전파속도 및 온도측정
 6. 결론
  6.1 연구 결과
  6.2 화재조사 착안사항
  6.3 제언
 실험협조 및 자문
 참고문헌

키워드

저자

• 김종북 [ Jong Buk Kim | 세종소방본부 ]

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  한국화재감식학회 학회지 [Magazine of Fire Investigation Socity of Korea]

• 간기

  계간

• pISSN

  2092-531X

• 수록기간

  2009~2026

• 등재여부

  KCI 등재

• 십진분류

  KDC 539 DDC 628