초록

영어

Nogime temmoku is a tea bowl which has crystal on the surface. It has brown pattern as like an ear of rice on the black background. Usually, this glaze of nogime temmmoku is used for tea bowl. For example, in case of Tenmoku produced in Japan, its plastic temperature is about 1290℃ and the time required for plasticity with the crystallization is about 35 hours, which result in high loss of time and economy. The purpose of this study is to identify how to solve this problem. That is, to reduce the plastic temperature to 1250〜1260℃ and the plasticization time to within 11〜12 hours as well as to simplify the schedule of plasticization. To achieve this purpose, development of new glaze should be conducted which is adequate in terms of plasticization time. In this study, the plasticization temperature has been fixed at 1250〜1260℃ to establish the composition and manufacturing procedure of the glaze from Tenmoku.

한국어

화천목이란 검은색 바탕에 갈색의 벼 이삭과 같은 침상 무늬가 결정으로 나타나는 다완을 의미한다. 주로, 다완에 시유 된 유약이다. 현재 일본에서 생산되는 화목 천목의 예를 들면 소성온도는 약 1290℃에서 소성시간이 약35시간 이상 소요되어 화목천목의 결정이 아름답게는 만들어지나 시간과 경제성 면에서 손실이 크다. 본 연구의 목적은 이와 같은 문제점을 해결하고자 하는 것이다. 즉, 소성 온도를 1250〜1260℃로 낮추며 소성시간은 약 11〜12시간 이내로 단축시킴과 동시에 소성 스케줄도 간편하게 하려는데 그 목적이 있다. 이와 같은 연구목적을 달성하기 위해서는 소성시간에 맞는 새로운 유약개발이 함께 수행되어야 하므로 본 실험에서는 소성온도를 1250〜1260℃로 고정시켜 놓고 화목 천목 유약의 조성과 제조공정을 확립하고자 하였다.

목차

개요
 Abstract
 Ⅰ. 서론
  1. 천목의 유래 및 배경
  2. 천목의 제조공정
  3. 연구 목적
 Ⅱ. 본론
  1. 실험소지
  2. 사용원료
  3. 유약조합
  4. 안료첨가실험
  5. 소성방법
  5. 소성방법
 Ⅲ. 유약 및 소성 결과고찰
  1. 화천목 유약 결과
  2. 화천목 제조에 안료 첨가 효과
  3. 고품질 화천목의 생산 조건
 Ⅳ. 결론
 도표 및 그림목록
 참고문헌

키워드

저자

• 정종혁 [ Jung Jong-Heuk | 정도가 도예 연구소 소장 ]

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  한국도자학연구 [The Jouranl of the Korean Society of Ceramic Art]

• 간기

  연3회

• pISSN

  1738-8473

• 수록기간

  2005~2023

• 등재여부

  KCI 등재

• 십진분류

  KDC 631 DDC 738