This study aims at identifying the variation of physicochemical properties for galena ore in order to use it in understanding of manufacturing techniques in terms of metallurgical method and smelting or refining process for obtaining lead. The ores in the study obtained from the operating mine have been washed and pre-treated for a test. Metallic lead has been extracted by roasting process. The result displays that galena is still in present in the matt despite of exposure to high temperature, over 1000℃. Nearly 11.1g/㎤ specific gravity metallic lead has been collected from the refining test of which aim was to remove the remnant galena and a trace of concentrated silver has been identified at the grain boundary. The result suggests that at least one refining process was essential to acquire high purity metallic lead and cupellation had been executed to remove remnant silver.

한국어

납을 획득하는 방법과 처리과정에서 일어나는 물리·화학적 거동변화를 확인함으로써 납이 함유된 고대 금속유물의 제작기법 연구에 활용하고자 방연석을 현재 가행 중인 광산에서 채취하여 세척 및 선광 등의 전처리 공정을 거쳐 제련 및 정련실험을 실시하였다. 실험결과, 납은 배소-화학반응에 의해 추출되며, 1,000℃이상의 고온에서도 방연석이 matte 내 존재하고 있음을 알 수 있었다. 이후 잔존하고 있는 방연석을 제거하기 위해 정련실험을 실시한 결과, 약 11.1g/㎤의 비중을 갖는 금속 납이 추출되었으며 방연석 내 미량으로 존재하고 있던 Ag가 입계 내에 응집되는 것을 확인하였다. 이를 통해 고순도의 납을 제작하기 위해서는 적어도 1번 이상의 정련 과정과 은을 제거하기 위한 회취법 등이 시행되었을 것이다.

목차

초록
 ABSTRACT
 1. 서론
 2. 연구방법
  2.1. 실험방법
  2.2. 분석방법
 3. 분석 결과
  3.1. 표면상태 분석 결과
  3.2. 단면 및 광학현미경관찰 결과
  3.3. 결정구조 분석결과
  3.4. 미세조직 및 성분분석 결과
  3.5. 미량원소 분석결과
  3.6. 비중 측정 결과
 4. 고찰
 5. 결론
 참고문헌

키워드

저자

• 한우림 [ Woo-rim Han | 국립문화재연구소 보존과학연구실 ]
• 김소진 [ So-jin Kim | 국립문화재연구소 보존과학연구실 ]
• 이은우 [ Eun-woo Lee | 국립문화재연구소 보존과학연구실 ]
• 황진주 [ Jin-ju Hwang | 국립문화재연구소 보존과학연구실 ]
• 김수기 [ Su-ki Kim | 용인대학교 문화재학과 ]
• 한민수 [ Min-su Han | 국립문화재연구소 보존과학연구실 ] Corresponding author

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  보존과학회지 [Journal of Conservation Science]

• 간기

  연5회

• pISSN

  1225-5459

• eISSN

  2287-9781

• 수록기간

  2003~2026

• 등재여부

  KCI 등재

• 십진분류

  KDC 602 DDC 700