Electrodes were fabricated based on activated carbon powder BP-20, conducting agent such as Super P, vapor grown carbon fiber (VGCF) and acetylene black (AB), and the mixed binders of flexible poly(vinylidenefluoridehexafluoropropylene) [P(VdF-co-HFP)] and cross linking dispersion agent of polyvinylpyrrolidone (PVP) to increase mechanical strength. According to impedance measurement of the electrode with the addition of conducting agent, we found that it was possible to charge rapidly by the fast steady-state current convergence due to low equivalent series resistance (AC-ESR, fast charge transfer rate at interface between electrode and electrolyte and low RC time constant. The self-discharge of unit cell showed that diffusion process was controlled by the ion concentration difference of initial electrolyte due to the characteristics of Electric Double Layer Capacitor (EDLC) charged by ion adsorption in the beginning, but this by current leakage through the double-layer at the electrode/electrolyte interface had a minor effect and voltages of curves were remained constant regardless of electrode material. We found that the 2.3V/230F grade EDLC would be applied to industrial safety usage such as uninterrupted power supply (UPS) because of the constant DC-ESR by IR drop regardless of discharge current.

목차

Abstract
 1. 서론
 2. 이론적 배경
 3. 실험방법
  3.1. 전극재료 및 기기
  3.2. 단위셀 제조
  3.3. 2.3V/3,000F급 EDLC 제작
 4. 실험 결과
  4.1. 단위셀의 전기화학적 특성
  4.2 2.3V/3,000F 급 EDLC의 전기화학적 특성
 5. 결론
 6. 참고문헌

저자

• 김경민 [ 명지대학교 화학공학과 ]
• 장인영 [ 명지대학교 화학공학과 ]
• 강안수 [ 명지대학교 화학공학과 ]

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  대한안전경영과학회 학술대회논문집

• 간기

  부정기

• 수록기간

  1999~2022

• 십진분류

  KDC 530 DDC 620