The influence of noxious corrosive gas, which is the product of fossil fuel, and the acidic descent material, which becomes the reason for such reaction, on wax which protects the cultural assets, and the habitat factor were researched. It could be viewed that corrosion occurred rapidly due to the acidic descent material, which have the long staying on the material, rather than harmful corrosive gas. Also, it could be figured out that such corrosion began from whitening phenomenon of coated wax. As the acidity increased, more whitening phenomenon occurred, and eventually, it could be found out that whitening effect began due to the acidic descent material, corrosive gas and various 0.1 M acid solution, which lead to the exposure of internal metal, and corrosion occurred. The wax with the greatest resistance to the acidity due to its least changing aspect seemed to be Renaissance wax, except sulfuric acid.

한국어

화석 연료의 생성물인 유해 부식 가스와 이들의 원인으로 나타나는 산성 강하물이 야외 銅 조형물을 보호하고 있는 왁스에 미치는 환경에 대한 영향성을 연구하였다. 부식이 유해 가스보다는 체류성이 강한 산성 강하물에 의해 급격히 진행되는 것으로 볼 수 있었으며, 이 부식의 시작이 코팅된 왁스의 백화 현상으로부터 시작되는 것을 알 수 있었다. 산성도가 증가할수록 백화 현상이 크게 발생하였으며 결과적으로 산성강하물 및 부식 가스에 의해 백화 현상의 시작으로 내부 금속의 노출 현상이 나타나게 되어 부식이 진행되는 것으로 알 수 있었다. 왁스가 코팅된 동 시편은 유해 부식 가스와 산성비, 0.1 M의 산들에 노출되었으며 이의 결과로 가장 변화가 적고 산성도에 대한 저항성이 큰 왁스로는 황산의 결과를 제외하고는 모든 실험에서 Renaissance wax의 변화가 가장 작은 것으로 나타났다.

목차

초록
 ABSTRACT
 1. 서론
 2. 실험
  2.1. 실험대상 및 시편 제작
  2.2. 실험방법
  2.3. 분석방법
 3. 결과 및 고찰
  3.1. 표면의 부식
  3.2. 표면 색상의 변화
  3.3. 표면 광택도의 변화
  3.4. 시편의 두께 변화
 4. 결론
 참고문헌

키워드

저자

• 오승준 [ Seung-jun Oh | 한국고고환경연구소 보존과학연구실 ]
• 위광철 [ Koang-Chul Wi | 한서대학교 ] Corresponding Author

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  보존과학회지 [Journal of Conservation Science]

• 간기

  연5회

• pISSN

  1225-5459

• eISSN

  2287-9781

• 수록기간

  2003~2026

• 등재여부

  KCI 등재

• 십진분류

  KDC 602 DDC 700