Earticle

초록

영어

In constructing a concrete structure, one of the most important things to be considered is the construction period, because delay in the construction period makes construction costs more expensive. This paper investigated the effects of the kinds and replacement ratio of mineral admixtures as fine aggregate on the early strength properties of mortar and concrete mixtures. For this purpose, fly ash(FA) and blast furnace slag powder(BS) which are broadly used as mineral admixtures in concrete were selected in this investigation. In addition, another mineral admixtures such as meta kaolin(MK), zeolite(ZL) and diatomite(DM), which have an improvement effect of strength were used. The mineral admixtures were used to replace fine aggregate at replacement ratios of 0%, 2% and 4% by volume. The compressive strength of mortar and concrete were determined at various early ages. In addition, the batcher plant(B/P) test was performed for optimum mixture selected through previous tests. Test results indicated that the dosage of high-range water reducing agent of the mixture using the mineral admixture as fine aggregate increased relatively, in particular, the dosage of the mixture using DM as fine aggregate increased significantly about 4 to 6 times than other mixtures. The early-age compressive strength of mortar and concrete mixtures with mineral admixture as fine aggregate was higher than that of base mixtures. In addition, the compressive strength of concrete with BS showed higher early strength value than other mixtures. For B/P test results, the time for deforming of early-strength development concrete(ESC) which ranged from 20 to 38 hours, was shorter than the Plain mixture ranging from 30 to 72 hours.

목차

Abstract
 1. 서론
 2. 실험개요
  2.1 실험계획
  2.2 사용재료 및 시험방법
 3. 실험결과 및 분석
  3.1 혼화재 종류 및 치환율에 따른 모르타르의 유동성 및 압축강도 발현특성(Ⅰ시리즈)
  3.2 혼화재 종류 및 치환율에 따른 콘크리트의 유동성 및 압축강도 발현특성(Ⅱ시리즈)
  3.3 레미콘 B/P시험을 통한 양생온도별 콘크리트의 조기강도 발현특성 (Ⅲ시리즈)
 4. 결론
 참고문헌

키워드

혼화재 플라이애시 메타카올린 고로슬래그미분말 잔골재 압축강도 Mineral Admixture Fly Ash Meta Kaolin Blast Furnace Slag Powder Fine Aggregate Compressive Strength

저자

• 최세진 [ Choi, Se-Jin | (주)삼표 기술연구소 책임연구원, 공학박사 ] Corresponding Author
• 김무한 [ Kim, Moo-Han | 충남대학교 건축공학과 명예교수, 공학박사 ]

참고문헌

발행기관

간행물