I investigated the homogeneous liquid crystal alignment using parallel patterning on nickel oxide thin film. Nickel oxide thin film was prepared by sol-gel process, which is and cost effective method to form oxide thin film. Since the sol-gel process is solution driven method, the patterning on nickel oxide can be achieved by imprinting lithography. Nickel oxide with parallel pattern was used for liquid crystal alignment layer, which can be a alternative to conventional rubbing process to aligning a liquid crystal molecules. As a result, a high transmittance of 83.9% was confirmed for the NiO film, and a stable horizontal orientation pretilt angle of 0.2° occurred in the imprinted NiO film. These results were judged to be a positive level that can be commercialized in the horizontal alignment type liquid crystal display that is currently used universally. Anisotropic characteristics of nickel oxide induced by a parallel pattern leads to the alignment of liquid crystals.

1차원 구조를 갖는 나노 와이어들은 나노 소자를 구현하기 위한 building-block으로 많은 과학자들의 주목을 받고 있고 또한 연구되고 있다. 하지만 그것을 정확하게 위치시키고 일정한 간격으로 정렬시키기 위한 기술 개발은 아직도 해결해야 할 큰 과제로 남아 있다. 이 논문에서, 우리는 ahsing 기술과 표면 패터닝 기술을 이용하여 대면적의 실리콘웨이퍼 위에 DNA(deoxyribonucleic acid)를 기반으로 한 금 나노 와이어를 정확하게 위치시키고 일정한 간격으로 정렬시킬 수 있는 새로운 제어 기술을 제안한다. 먼저 우리는 포토 리소그래피 공정과 $O_2$ 플라즈마 ashing 기술을 이용하여 선폭을 100 nm로 감소 시켰다. 그리고 자기조립단분자막 (self-assembled monolayers; SAMs) 방법과 lift-off 공정을 반복함으로서 1-octadecyltrichlorosilane(OTS) 층과 aminopropylethoxysilane(APS) 층을 형성하였다. 마지막으로 DNA 용액을 샘플 표면 위에 도포하고 분자 빗질 방법으로 DNA를 한 방향으로 정렬 시켰고 금 나노입자 용액을 처리하였다. 그 결과 금 나노 와이어는 $10{\mu}m$ 간격으로 일정하게 정열 되었고, APS 층에만 정확하게 정렬되었다. 우리는 금 나노 와이어를 관찰하기 위하여 원자간력 현미경 (Atomic Force Microscope AFM)을 사용하였다.