지르코니아 세라믹의 Glass-infiltration에 의한 2축 굽힘강도에 관한 연구
Study on Biaxial Flexural Strength by Glass-infiltration of Zirconia Ceramics
-
- 발행기관
- 대한치과기공학회 바로가기
-
- 간행물
- 대한치과기공학회지 바로가기
-
- 통권
- Vol.30 No.1 (2008.07)바로가기
-
- 페이지
- pp.41-47
-
- 저자
-
- 언어
- 한국어(KOR)
-
- URL
- https://www.earticle.net/Article/A89899
※ 기관로그인 시 무료 이용이 가능합니다.
4,000원
원문정보
초록
- 영어
- This study was to evaluate the biaxial flexural strength of zirconia ceramics after glass-infiltration on zirconia core.
The zirconia specimens were made with diameter-15mm, thickness-0.6mm using zirconia block which divided into 1) sintered group, 2) heat - treated group, 3) Glass - infiltrated group and experimented fracture strength by each 10 specimens in experimental group. The biaxial flexural test was performed at crosshead speed of 0.1ᒠmin.
The experiment result average fracture strength was shown 541.0ßÁ in sintered group and glass-infiltrated group as 662.2ßÁ river of 22.4% rise appear. Weibull coefficient sintered group is 3.462 and glass-infiltrated group improved believability about fracture strength from melting permeation processing of glass by 4.716.
목차
Abstract
Ⅰ. 서론
Ⅱ. 재료 및 방법
1. 봉규신염 글라스 제조
2. 시편의 제작
3. 2축 굽힘시험
4. 피절강도의 통계적 분석
Ⅲ. 결과
Ⅳ. 고찰
Ⅴ. 결론
참고문헌
키워드
Biaxial Flexural Strength Glass-infiltration of Zirconia Ceramics.저자
간행물 정보
발행기관
-
- 발행기관명
- 대한치과기공학회 [The Korean Academy Of Dental Technology]
- 설립연도
- 1979
- 분야
- 의약학>치의학
- 소개
- 본 학회는 치과기공에 관한 모든 분야의 연구와 회무를 총괄하기 위하여 세분화된 분과학회의 회원 상호간 학술교류와 정보를 수집하고, 보수교육 및 학술대회 준비, 진행과 학회지 발간등의 업무를 효율적으로 수행함을 목적으로 한다.
간행물
-
- 간행물명
- 대한치과기공학회지 [THE JOURNAL OF KOREAN ACADEMY OF DENTAL TECHNOLOGY]
- 간기
- 계간
- pISSN
- 1229-3954
- eISSN
- 2288-5218
- 수록기간
- 1979~2026
- 등재여부
- KCI 등재
- 십진분류
- KDC 515 DDC 617
이 권호 내 다른 논문 / 대한치과기공학회지 Vol.30 No.1
피인용수 : 0건 (자료제공 : 네이버학술정보)
함께 이용한 논문 이 논문을 다운로드한 분들이 이용한 다른 논문입니다.
출처 : 네이버학술정보
0개의 논문이 장바구니에 담겼습니다.