In hydrothermal reaction tests, smectite-to-illite conversion was identified using a domestic bentonite which is favorably considered as a buffer material, and its dependency on various hydrothermal conditions was investigated. The analysis results of the XRD and Si concentration indicated that the smectite-to-illite conversion was a major process of bentonite alteration under the hydrothermal conditions. The temperature, potassium concentration in solution, and pH were observed to significantly affect the smectite-to illite conversion. A model of conversion reaction rate was suggested to evaluate the long-term stability of smectite composing a major constituent of bentonitic buffer. It was expected from the evaluation results that the smectite would keep its integrity for very long disposal time under a normal condition, whitens it might be converted to illite by 50 percent after over year of disposal time under a conservative condition and consequently lose its swelling capacity as a buffer material of a repository.

한국어

벤토나이트 완충재의 열수거동 실험에서는 고준위폐기물처분장 완충재로 유력하게 고려되고 있는 국산 벤토나이트를 대상으로 열수특성을 규명하고, 또 그 결과를 바탕으로 KRS 처분환경에서 벤토나이트 완충재의 장기건전성을 평가하였다. 실험결과, 벤토나이트 완충재의 열수반응은 주 구성광물인 스멕타이트의 일라이트화를 통해 진행되었으며, 온도, 농도, pH는 이러한 일라이트화에 중요한 열수반응인자 역할을 하였다. KRS 처분환경에 대한 국산벤토나이트 완충재의 장기건전성을 분석한 결과, 정상상태에서는 벤토나이트 완충재가 오랜 기간 동안 방벽재기능을 유지하였지만, 보수적인 조건에서는 약 년이 경과했을 때 벤토나이트 완충재를 구성하는 스멕타이트의 50%이상이 일라이트로 전환되어 방벽재로서의 팽윤능력을 상실할 수 있음을 예상할 수 있었다.

목차

Abstract
 요약
 I. 서론
 II. 실험
  가. 모의용액 제조
  나. 추출용매 제조
  다. 실험 방법
  라. 분석
 III. 실험 결과 및 고찰
  가. 제 3상 형성
  나. 질산 추출
  다. Tc, Np 및 U의 공추출
  라. Tc, Np 및 U의 수차분리
  마. 분리 계수(separation factor)
 IV. 결론
 참고문헌

키워드

저자

• 이재완 [ 조원진 | 한국원자력연구원 ]
• 조원진 [ Won Jin Cho | 한국원자력연구원 ]

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  방사성폐기물학회지 [Journal of Nuclear Fuel Cycle and Waste Technology (JNFCWT)]

• 간기

  계간

• pISSN

  1738-1894

• 수록기간

  2003~2017

• 십진분류

  KDC 559 DDC 629