The physical property and phase transformation in a commercial dental casting high gold alloy was investigated as a function of ageing temperature and time usingmicrovickers hardness tester, X-ray diffraction, optical and electron microscopy andEPMA analyser. 1. With increasing ageing time, the hardness of solution-treated gold alloys increasedslowly at the initial stage of ageing treatment at an ageing temperature of 300~400℃,and it reached a maximum value of hardness at the medium stage. Finally, it decreasedgradually during further ageing. The maximum value of hardness at was similar with thatof the conventional materials and suitable for using as the crown & bridge. 2. During isothermal ageing at a temperature range of 300~400℃, three phasesconsisting of the Au-rich α₁phase with a face-centered cubic structure, the Pt3Zn α₂phasewith an ordered AuCu3(L12) type(f.c.c.) and the Pt-rich α₃phase with face-centered cubicstructure in solution-treated gold alloys were transformed into different three phasesconsisting of the α₁phase, the α₃phase and the PtZn βphase with an ordered AuCu I(L10)type. 3. The hardening of gold alloys was attributed to the lattice strains of the matrixresulting from the transformation of the α₂phase to the βphase.4. The softening of gold alloys during over-ageing was attributed to the coarsening ofthe nodules consisting of the βphase and α₁matrix.

목차

Abstract
 Ⅰ. 서론
 Ⅱ. 재료 및 방법
  1. 실험합금
  2. 열처리
  3. 경도 시험
  4. X선회절 실험
  5. 금속현미경 및 주사전자현미경 관찰
  6. 전자탐침 미소분석
 Ⅲ. 실험 결과
  1. 경도 시험
  2. X선회절 도형
  3. 금속현미경및주사전자현미경관찰
  4. 전자탐침 미소분석
 Ⅳ. 고찰
 Ⅴ. 결론
 <참고문헌>

키워드

저자

• 이희경 [ Hee-Kyung Lee | 대구보건대학 치기공과 ]
• 박명호 [ Myoung-Ho Park | 대구보건대학 치기공과 ]
• 이화식 [ Hwa-Sik Lee | 대구보건대학 치기공과 ]

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  대한치과기공학회지 [THE JOURNAL OF KOREAN ACADEMY OF DENTAL TECHNOLOGY]

• 간기

  계간

• pISSN

  1229-3954

• eISSN

  2288-5218

• 수록기간

  1979~2026

• 등재여부

  KCI 등재

• 십진분류

  KDC 515 DDC 617