도재소부용 금속구조물의 강화방법
Strengthening method of a porcelain fusedAu-Pt-Cu-0.5In alloy
-
- 발행기관
- 대한치과기공학회 바로가기
-
- 간행물
- 대한치과기공학회지 바로가기
-
- 통권
- Vol.25 No.1 (2003.07)바로가기
-
- 페이지
- pp.63-70
-
- 저자
-
- 언어
- 한국어(KOR)
-
- URL
- https://www.earticle.net/Article/A45759
※ 기관로그인 시 무료 이용이 가능합니다.
4,000원
원문정보
초록
- 영어
- The microstructure and hardness of a porcelain fused Au-Pt-Cu-In alloy was investigated usingoptical microscopy, secondary electron microscopy, electron probe microanalyzer, transmissionelectron microscope, and vickers hardness. The hardness of the heat-treated Au-Pt-Cu-Inquartenary alloy reached a maximum value in 30 min at 550in the range of 150 to 950. In theaged Au-Pt-Cu-0.5In alloy at 550, the hardness of the alloy rapidly increased until 30min withincreasing aging time and after that it was remained nearly constant value. Based on above results, glazing and final aging of the porcelain fused Au-Pt-Cu-0.5In alloy wereperformed at 920 and 550, respectively. The hardness of Au-Pt-Cu-0.5In alloy glazed at 920was 90 Hvand that of the alloy aged for 30 min at 550increased to 160 Hv. This indicates that aceramic-metal crown with high strength can be manufactured using the glazing at 920andfollowed final aging at 550for 30 min.
목차
Abstract
Ⅰ. 서론
Ⅱ. 시편제작 및 실험방법
Ⅲ. 결과 및 고찰
1. 기계적 성질
2. 미세조직관찰
3. 상분석
Ⅳ. 결론
참고문헌
키워드
Au-Pt-Cu-0.5 In alloy ceramic-metal crown glazing aging high strength.저자
간행물 정보
발행기관
-
- 발행기관명
- 대한치과기공학회 [The Korean Academy Of Dental Technology]
- 설립연도
- 1979
- 분야
- 의약학>치의학
- 소개
- 본 학회는 치과기공에 관한 모든 분야의 연구와 회무를 총괄하기 위하여 세분화된 분과학회의 회원 상호간 학술교류와 정보를 수집하고, 보수교육 및 학술대회 준비, 진행과 학회지 발간등의 업무를 효율적으로 수행함을 목적으로 한다.
간행물
-
- 간행물명
- 대한치과기공학회지 [THE JOURNAL OF KOREAN ACADEMY OF DENTAL TECHNOLOGY]
- 간기
- 계간
- pISSN
- 1229-3954
- eISSN
- 2288-5218
- 수록기간
- 1979~2026
- 등재여부
- KCI 등재
- 십진분류
- KDC 515 DDC 617
이 권호 내 다른 논문 / 대한치과기공학회지 Vol.25 No.1
피인용수 : 0건 (자료제공 : 네이버학술정보)
함께 이용한 논문 이 논문을 다운로드한 분들이 이용한 다른 논문입니다.
출처 : 네이버학술정보
0개의 논문이 장바구니에 담겼습니다.