초록

영어

The purpose of this study was to process bio-active glass ceramic composite, reinforced withsapphire fibers, by hot press. Also to study the interface of the matrix and the sapphire fiber, andthe mechanical properties.Glass raw materials melted in Pt crucible at 1300during 3.5 hours. The melt was crushed inball mill and then crushed material, ground and sieved to <40ß. Sapphire fibers cut (30) andaligned.Powder and fibers hot pressed.The micrographs show good bonding between the matrix and the fiber and no porosity in theglass matrix. This means ideal fracture phenomena. Glass is fractured before the fiber. This isindication of good fracture strength.EDXS showing aluminum rich phase and crystalline phase. Bright field image of the matrixshowing crystalline phase.Also diffraction pattern of TEM showing the crystalline phase and more than one phase.Strength of the samples was determined by 3 point bend testing. Strength of the 10vol% samplewas approximately 69MPa, while strength of the control sample is 35MPa.Conclusions through this study as follow: 1. Micrographs show no porosity in the glass matrix and the interface. 2. The interface between the fiber and the glass matrix show no gaps. 3. Fracture of the glass indicates characteristic fiber-matrix separation. 4. Presence of crystalline phase at high processing temperature. 5. Sapphire is compatible with bioactive glass.

목차

Abstrac
 Ⅰ. 서론
 Ⅱ. 실험방법
  1. Bioactive Glass 복합재료 제작
  2. 샘플준비
  3. 복합재료 제작
  4. 시험편 제작과 실험
 Ⅲ. 결과 및 고찰
  1. Bioactive Glass복합재료의 특성
  2. 고찰
 Ⅳ. 연구결과
 참고문헌

키워드

저자

• 김부섭 [ Bu-sob, Kim | 부산가톨릭대학교 보건과학대학 치기공학과 ]

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  대한치과기공학회지 [THE JOURNAL OF KOREAN ACADEMY OF DENTAL TECHNOLOGY]

• 간기

  계간

• pISSN

  1229-3954

• eISSN

  2288-5218

• 수록기간

  1979~2026

• 등재여부

  KCI 등재

• 십진분류

  KDC 515 DDC 617