초록

영어

Cobalt oxide (Co3O4ㆍCoO) ultra fine particles were synthesized by liquid phase precursor method. cobalt(II) chloride hexahydrate (CoCl2ㆍ6H2O) was as a starting material. A plant-derived crystalline cellulose was used as impregnating materials. A impregnated precursor was calcined at a temperature of 350 to 900°C to obtain cobalt oxide particles having a particle size of 1 to 10μm. The crystallization process and morphology according to the calcination temperature were examined, and the properties of the synthesized powder were evaluated using SEM and XRD. It was confirmed that a crystal phase of Co3O4 began to form around 350°C and crystal growth occurred up to 900°C. At a temperature above 500°C, the Co3O4 crystal was changed to another crystal phase CoO.

한국어

CoCl2ㆍ6H2O 수용액을 결정성셀룰로오스에 함침시켜 건조한 후, 하소, 소성을 통하여 산화코발트(Co3O4ㆍCoO) 초미세입 자를 합성하였다. 합성된 코발트 산화물 입자의 결정구조 및 표면구조를 주사전자현미경(SEM)과 X-선회절분석(XRD)으로 조 사하였다. CoCl2ㆍ6H2O 수용액을 함침시키는 매개체로 사용한 결정성셀룰로오스(crystalline cellulose)는 470°C 정도에서 열분 해 되었고, Co3O4 결정상은 350°C에서 생성되기 시작하였다. Co3O4 결정상은 500°C까지 유지되었으며, 500°C 이상의 온도에서 는 CoO 결정상으로 변화하는 것을 알 수 있었다. 열처리 온도가 증가함에 따라 산화코발트 입자의 크기가 커지는 현상이 나타 났으며, 900°C 이상의 온도에서는 입자간 용융이 일어나는 것이 관찰되었다. 하소온도 700°C 이하의 온도에서 입자크기 2-10μ m의 Co3O4와 CoO의 초미세입자가 생성되는 것을 확인하였다.

목차

요약
Abstract
Ⅰ. 서론
Ⅱ. 실험
1. 산화코발트의 합성
2. 분석
Ⅲ. 결과 및 고찰
Ⅳ. 결론
References

키워드

저자

• 김수종 [ Soo-Jong Kim | 정회원, 한라대학교 신소재화학공학과 교수 ] 제1저자

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  The Journal of the Convergence on Culture Technology (JCCT) [문화기술의 융합]

• 간기

  격월간

• pISSN

  2384-0358

• eISSN

  2384-0366

• 수록기간

  2015~2025

• 등재여부

  KCI 등재

• 십진분류

  KDC 600 DDC 700