Earticle

초록

영어

This study analyzed the microstructures and chemical composition of three samples of bronze mirrors excavated in the Jeollanam-do region, particularly Goheung and Damyang. Under x-ray irradiation, the analysis results confirmed the broken parts and pores caused by cracks, casting, and corrosion. Major and minor elemental analysis were performed on three mirrors by Scanning electron microscopy (SEM) with Energy dispersive x-ray spectrometry (EDS) and Inductively coupled plasma mass s pe ctrometry ( ICP-MS). T he re sult s hows t hat t he b ronze mirrors c ontained C u-Sn-Pb a lloys. Alpha phase and eutectic phase were observed in the microstructure, confirming that the casting was performed without additional heat treatment. Notably, Three bronze mirrors were made early Three Kingdoms period in Korea.

한국어

본 연구는 전라남도 고흥과 담양지역에서 출토된 청동거울의 금속학적 분석으로 제작 방법을 확인하고자 하였다. 연구한 대상 유물은 담양 제월리 고분에서 출토된 청동거울 2점, 고흥 봉룡리에서 발견된 청동거울 1점으로 총 3점이다. 분석 결과 X선을 이용한 조사에서 육안 으로 관찰되지 않던 균열과 부식으로 인해 발생된 결실부와 주조제작으로 인해 형성된 기공을 확인할 수 있었다. 청동거울의 주성분은 Cu-Sn-Pb이며 Cu 73∼79 wt%, Sn 17∼21 wt%, Pb 3∼4 wt%로 2 wt% 이상의 Pb이 포함되어 있어 청동거울에 필요한 주조성 및 기계적 성질을 조절하 기 위한 것으로 확인된다. 또한 미세조직 관찰 결과 주조한 상태에서 추가적인 열처리가 이루 어지지 않은 α상과 α+δ공석상의 조직으로 비교적 이른 시기에 제작된 삼국시대 청동거울로 추정할 수 있다.

목차

초록
ABSTRACT
1. 서론
2. 분석대상 및 방법
2.1. 유적 및 분석대상
2.2. 분석 방법
3. 분석 결과
3.1. 방사선 비파괴 조사
3.2. 성분 분석
3.3. 미세조직 분석
4. 고찰
5. 결론
사사
REFERENCES

키워드

저자

• 이은지 [ Eun Ji Lee | 국립나주문화재연구소 ] Corresponding Author

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  보존과학회지 [Journal of Conservation Science]

• 간기

  연5회

• pISSN

  1225-5459

• eISSN

  2287-9781

• 수록기간

  2003~2026

• 등재여부

  KCI 등재

• 십진분류

  KDC 602 DDC 700