Purpose: This study aimed to identify the impact of physical surface roughing with a polishing tool onto the pre-sintering yttria-stabilized tetragonal zirconia polycrystals (TZP) core and liner treatment for chemical bonding on the bond strength of TZP core and veneering ceramic. Methods: Overall, 80 specimens were classified into two groups (non-liner, NL; and usingliner, UL ) depending on the use of liner, and these two groups were then subclassified into four groups depending on the polishing tool used. (1) Non-liner groups: NS, non-liner+stone point; NC, non-liner+carbide bur; NP, non-liner+paper cone point; NT, non-liner+silicon point. (2) Using-liner groups: US, using-liner+stone point; UC, using-liner+carbide bur; UP, usingliner+ paper cone point; UT, using-liner+silicon point. The pre-sintering surface roughing values and shapes were observed, and after burning up the veneering ceramic, the shear bond strength was measured using a universal testing machine. For significance testing, a oneway analysis of variance and Tukey’s multiple comparison test were conducted. An optical microscope was used to observe the fracture plane, and the following results were obtained. Results: Surface roughness NP (4.09±0.51 μm) represented a higher value than other groups (p<0.001). In shear bond strength, NS (35.21±1.44 MPa) of the NL group showed the highest bond strength (p<0.001). The UL group did not show a statistically significant difference between groups (p=0.612). Conclusion: Our study findings reveal that the bond strength of TZP core and veneering ceramic was improved by pre-sintering physical surface treatment than by chemical bonding with liner surface treatment.

목차

Abstract
INTRODUCTION
MATERIALS AND METHODS
1. 시편 준비
2. 표면 형상 및 거칠기 평가
3. 전단결합강도 및 파단면 분석
RESULTS
1. 표면 거칠기 특성
2. 전단결합강도
3. 파단면 분석
DISCUSSION
CONCLUSIONS
CONFLICT OF INTEREST
ORCID
REFERENCES

키워드

저자

• 이광영 [ Gwang-Young Lee | 원광보건대학교 치기공과 ]
• 홍민호 [ Min-Ho Hong | 부산가톨릭대학교 보건과학대학 치기공학과 ] Corresponding Author

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  대한치과기공학회지 [THE JOURNAL OF KOREAN ACADEMY OF DENTAL TECHNOLOGY]

• 간기

  계간

• pISSN

  1229-3954

• eISSN

  2288-5218

• 수록기간

  1979~2026

• 등재여부

  KCI 등재

• 십진분류

  KDC 515 DDC 617