Earticle

초록

영어

The purpose of this study was to develop high quality dark film honeycomb fabric curtains. The results of producing the prototype for various color tone development, hot melt viscosity, and adhesiveness test for the final prototype were as follows. The hexagonal honeycomb structure is easy to manufacture, has a good coupling force, and has a dark honeycomb fabric curtain. The hot melt condition was obtained with 540g of hot melt and 1.5kg of diluent, 242.3cp, and the curing result was obtained at 140°C. Seven different colors were developed using yellow, red, blue, and white four primary colors. The adhesive force test device was designed to enable more than 5,000 real tests by the automatic opening and closing device for the convenience of the field workers. The size of the test sample was designed to be 1,000mm × 1,200mm. As a result of designing and manufacturing the prototype to attach the monitor and the control device to automatically count, the prototype was made to be measured 10,000 times. The combined force of the honeycomb fabric curtain was maintained after 5,000 tests on the manufactured rock film honeycomb fabric curtain.

목차

Abstract
1. 서론
2. 실험 및 방법
2.1 기존 제품 문제점
2.2 암막 허니콤 패브릭 설계
2.3 핫 멜트의 점성 측정
2.4 다양한 색조 개발 및 색차 측정
2.5 허니콤 패브릭 접착력 테스트 장치 설계
3. 실험 결과
3.1 암막 허니콤 패브릭 설계 및 제작
3.2 핫 멜트의 점성 측정 결과
3.3 다양한 색조 개발 및 색차 측정 결과
3.4 허니콤 패브릭 접착력 측정 시제품 개발
4. 결론
후기
References

키워드

허니콤 커튼 접착력 원단 뒤틀림 핫 멜트 점도 Honeycomb Curtain Adhesion Fabric Twist Hot melt Viscosity

저자

• 원대희 [ Dae-Hee Won | Member, Wonkwang University, National Program of Excellence in Software SW Education Innovation Center, Assistant Professor ] Corresponding author

참고문헌

발행기관

간행물