In this study, the effects of the compaction method for (Mg+2B) powders on the apparent density and superconducting properties of MgB2 bulk superconductor were investigated. The raw powders used in this study were nano-sized boron (B) and spherical magnesium (Mg). A batch of a powder mixture of (Mg+2B) was put in a steel mold and uniaxially pressed at 1 ton or 3 tons into pellets. Another batch of the powder mixture was uniaxially pressed at 1 ton and then pressed isostatically at 1800 kg/cm2 in the water chamber. All pellets were heat-treated at 650℃ for 1 h in flowing argon gas for the formation of MgB2. The apparent density of powder compacts pressed at 3 ton was higher than that at 1 ton. The cold isostatic pressing (CIP) in a water chamber allowed further increase of the apparent density of powder compacts, which influenced the pellet density of the final products (MgB2). The compaction methods (uniaxial pressing and CIP) did not affect the formation of MgB2 and superconducting critical temperature (Tc) of MgB2, but affected the critical current density (Jc) of MgB2 significantly. The sample with the high apparent density showed high Jc at 5 K and 20 K at applied magnetic fields (0-5 T).

목차

Abstract
1. 서론
2. 실험과정
3. 결과 및 고찰
4. 결론
ACKNOWLEDGMENT
REFERENCES

키워드

저자

• M. O. Kang [ Korea Atomic Energy Research Institute, Daejeon, Korea, Sungkyunkwan University, Suwon, Korea ]
• J. Joo [ Sungkyunkwan University, Suwon, Korea ]
• B.-H. Jun [ Korea Atomic Energy Research Institute, Daejeon, Korea ]
• K. N. Choo [ Korea Atomic Energy Research Institute, Daejeon, Korea ]
• C.-J. Kim [ Korea Atomic Energy Research Institute, Daejeon, Korea ] Corresponding Author

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  한국초전도·저온논문지 (구 한국초전도저온공학회논문지) [Progress in Superconductivity and Cryogenics]

• 간기

  계간

• pISSN

  1229-3008

• eISSN

  2287-6251

• 수록기간

  1999~2026

• 등재여부

  KCI 등재,SCOPUS

• 십진분류

  KDC 427 DDC 537