In the industry, Zn galvanizing on the steel using the principle of sacrificial anode is used. The steel have some problem, specially corrosion problem. To solve corrosion problem, Zn-Mn alloy plating has been studied as one of the measures to increase the corrosion resistance rather than pure zinc plating. It is possible to be applied to automotive parts requiring high corrosion resistance even though the plating cost is high. In this study, Zn-Mn alloys were electrodeposited from an acidic chloride bath. The influence of the electrolytic conditions on the composition of the alloy plating in the chloride bath was investigated. As the current density of the cathode increases, Zn content of electrodeposit decrease and Mn content of electrodeposit increase. As the temperature of the electrolyte increases, Zn content of electrodeposit decrease and Mn content of electrodeposit increase. The results are explained by the cathode overvoltage curve of Mn and Zn.

한국어

강의 부식을 방지하기 위해서 희생양극의 원리를 이용한 아연도금이 사용된다. 순수아연도금은 몇가지 문제점을 가지고 있어 얇으면서 내식성을 증가시키기 위한 방안의 하나로 Zn-Mn 합금도금이 연구되어지고 있다. Zn-Mn 합금도금은 도금 단가가 높음에도 불구하고 고내식성을 요구하는 자동차 부품 등에 적용이 가능하다. 본 연구에서는 산성 염화용액에서 Zn-Mn 합금도금을 전착하였다. 이때 염화욕에서 합금도금의 조성에 미치는 전해조건의 영향을 조사하였다. 전류밀도가 증가함에 따라 Zn함량이 감소하고 Mn함량은 증가하였다. 전해액의 온도가 증가함에 따라 Zn함량이 감소하고 Mn함량은 증가하였으며, 음극 분극곡선을 가지고 결과를 설명하였다.

목차

요약
 Abstract
 1. 서론
 2. 실험방법
 3. 시험결과 및 고찰
  3.1 전류밀도의 영향
  3.2 온도의 영향
  3.3 표면형상
  3.5 고찰
 4. 결론
 REFERENCES

키워드

합금도금 아연도금 내식성 음극과전압 전착인자 Zn-Mn Zn-Mn alloy plating Zn plating corrosion property cathode overvoltage deposition parameters

저자

• 강수영 [ Soo Young Kang | 인하공업전문대학교 금속재료과 교수 ] Corresponding author

참고문헌

발행기관

간행물