Earticle

초록

영어

An accurate method to measure shielding effectiveness(SE) of EMI spray coating film is presented. After high frequency simulating, Circular coaxial standard test fixture is fabricated. A sample of EMI spray coating film was fabricated for insertion into a circular coaxial standard test fixture. The measuring instrument used an Agilent 8722ES vector network analyzer for the SE measurement. The exact SE of copper and silver mixed spray coating sample was measured by the composition of the measuring instrument and the measuring sample. The SE of copper sample was measured at 70 dB and the SE of copper and silver mixed spray coating sample was measured at 60 dB. As a result of the measurement, the reliability of the circular coaxial standard test fixture was confirmed.

한국어

EMI 스프레이 코팅막의 차폐효과(Shield Effectiveness, SE)를 측정하기 위한 정확한 방법을 제안하였다. 고주파 시뮬레이션을 한 후에 원형 동축 표준 측정기를 제작하였다. 원형 동축 표준 측정기에 삽입하기 위하여 EMI 스프레이 코팅막의 시료를 가공하였다. 차폐효과 측정을 위한 측정기는 에이질런트 8722ES 벡터 네트워크 분석기를 이용하였다. 이러한 측정기와 측정시료의 구성으로 구리와 은의 혼합 스프레이 코팅 시료의 정확한 차폐효과를 측정하였다. 동박 시료의 차폐효과는 70 dB로 측정되었고, 구리와 은의 혼합 스프레이 코팅 시료의 차폐효과는 60 dB로 측정되었다. 이와 같은 측정 결과로 원형 동축 표준 측정기의 신뢰성을 확인하였다.

목차

요약
 Abstract
 Ⅰ. 서론
 Ⅱ. 측정기의 시뮬레이션
 Ⅲ. 측정기 및 측정 시료의 제작
 Ⅳ. EMI 코팅막의 차폐 실험 결과
 Ⅴ. 결론
 References

키워드

저자

• 허정 [ Jung Hur | 정회원, 건국대학교 전기전자공학부 ]
• 이원희 [ Won-Hui Lee | 정회원, 서일대학교 정보통신공학과 ] 교신저자

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  한국인터넷방송통신학회 논문지 [The Journal of the Institute of Internet, Broadcasting and Communication]

• 간기

  격월간

• pISSN

  2289-0238

• eISSN

  2289-0246

• 수록기간

  2001~2025

• 십진분류

  KDC 326 DDC 380