Jiǔdiàn iron production site in China is a relic smelting site, which in the past produced pig iron. In this study, scientific analysis of the smelting furnace and collected slag was conducted to reveal some aspects of the ancient Chinese smelting technique. A 3D model of the smelting furnace showed a narrow lower part and an upper section which increased in diameter upwards. Although the smelting furnace relic does not include the upper part and its complete shape cannot be predicted, the remaining part suggests that the furnace had a larger diameter in the central part compared to the upper and lower parts. Most of the collected slag was completely vitrified. Long prismatic fayalite was observed in the matrix of some samples. The iron particles contained phosphorus, which could not be discharged during smelting work. In addition, as the CaO/SiO2 ratio was 0.42 or lower in the results of the content analysis, no CaO slag former had been added. However, the ratio of CaO/SiO2 to Al2O3/SiO2 did not have a constant trend. This needs to be investigated in a further study.

목차

ABSTRACT
 1. INTRODUCTION
 2. SUBJECTS AND METHODS
  2.1. Study subjects
  2.2. Study method
 3. RESULTS
  3.1. 3D modeling
  3.2. Main components
  3.3. Microstructure
 4. DISCUSSION AND CONCLUSION
 Acknowledgement
 REFERENCES

키워드

저자

• Chae Rin Bae [ Department of Cultural Heritage Conservation Sciences, Kongju National University, Gongju, 32588, Korea ]
• Nam Chul Cho [ Department of Cultural Heritage Conservation Sciences, Kongju National University, Gongju, 32588, Korea ] Corresponding author
• Young Hoon Jo [ Department of Cultural Heritage Conservation Sciences, Kongju National University, Gongju, 32588, Korea ]
• Jianli Chen [ School of Archaeology and Museology, Peking University, Beijing, 100871, China ]

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  보존과학회지 [Journal of Conservation Science]

• 간기

  연5회

• pISSN

  1225-5459

• eISSN

  2287-9781

• 수록기간

  2003~2026

• 등재여부

  KCI 등재

• 십진분류

  KDC 602 DDC 700