영어

Separation technology combining adsorption and membrane is expected to be applied in many fields such as water treatment. In this fusion technique, a functional carbon membrane having a carbon whisker grown on the surface of the membrane was developed to inhibit membrane fouling, which is a problem in the membrane separation process. In this study, to elucidate the mechanism of manufacturing the functional carbon membrane, the membrane was pretreated with the polymer latex of each mixing ratio and the membrane was formed by the CVD (Chemical Vapor Deposition) method. The membrane was analyzed by scanning electron microscope (SEM), CHN analyzer (Elemental Analyzer), and X-ray diffraction (XRD). As a result, the diameter and density of carbon whiskers were higher in case of polyvinyl di-chloride (PVdC): polyvinyl chloride (PVC) = 4.5: 55. It seems possible to control the diameter and density of the carbon whiskers according to the hydrogen content of the polymer latex.

한국어

흡착과 막을 융합시킨 분리기술은 수처리와 같은 환경 분야에서 많은 응용이 기대된다. 이 융합기술에 막분리 공정에서 문제가 되는 막 fouling을 억제시키기 위해 막표면에 카본휘스커를 성장시킨 기능성 카본막을 개발하였다. 본 연구에서는 기능성 카본막의 제조 Mechanism을 밝히기 위해, 각각의 혼합비율인 폴리머라텍스로 전처리를 하고 CVD(Chemical Vapor Deposing)법에 따라 막을 제조하였다. 이 막을 주사전자현미경(Scanning Electron Microscope(SEM)), CHN분석기(Elemental Analyzer), X-선회절법(X-Ray Diffraction(XRD))으로 분석하였다. 그 결 과 3번막(PVdC(PolyVinyl di-Chloride):PVC(Polyvinly Chloride)=4.5:55)의 경우가 카본휘스커의 직경과 밀도가 높았 다. 이것은 폴리머라텍스의 수소함유량에 따라 카본휘스커의 직경과 밀도를 조절하는 것이 가능할 것으로 보인다.

목차

요약
 Abstract
 Ⅰ. 서론
 Ⅱ. 연구방법
  1. 실험방법
  2. 분석방법
 Ⅲ. 결과 및 고찰
  1. 분석결과
 Ⅳ. 결론
 References

키워드

저자

• 배상대 [ Sang-Dae Bae | 정회원, 신라대학교 화학공학과 ] Corresponding author

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  The Journal of the Convergence on Culture Technology (JCCT) [문화기술의 융합]

• 간기

  격월간

• pISSN

  2384-0358

• eISSN

  2384-0366

• 수록기간

  2015~2025

• 등재여부

  KCI 등재

• 십진분류

  KDC 600 DDC 700