BASIC STUDY FOR APPLICATIONS AND PHYSICAL PROPERTIES CHANGE BY SURFACE TREATMENT OF MAGNESIAUM ALLOY (AZ31)

첫 페이지 보기
  • 발행기관
    국제과학영재학회 바로가기
  • 간행물
    APEC Youth Scientist Journal 바로가기
  • 통권
    Vol. 7 No.1 (2015.01)바로가기
  • 페이지
    pp.31-44
  • 저자
    Gu Min KANG, Jin Sol KIM, Jun Hyeok LIM
  • 언어
    영어(ENG)
  • URL
    https://www.earticle.net/Article/A328970

※ 기관로그인 시 무료 이용이 가능합니다.

4,600원

원문정보

초록

영어
Magnesium alloy is a light material but has a strong characteristic. However, its high corrosive and monotonous color interrupts the magnesium alloy from commercialization. In this research we have studied the process of improving magnesium corrosion and its esthetic function. After the process for cleaning and etching, the magnesium alloy was put on a panel and ultrapure water on Teflon airtight container, and then heated in a specific condition. After that, the change of color at the surface was observed. It was found out that the surface color changed after it was heated in a dye. Besides, Lauric acid is widely known in improving the hydrophobic property. We observed it on a specific condition, and the result shows that higher contact angle appeared above the surface when it was heated in high temperatures and for longer times. Subsequently it improved its higher hydrophobicity. The tensile strength was measured by 11.0 Mpa in this result. It was found that this research can be used as a basic data on the development of magnesium components and materialize color.

목차

ABSTRACT
 1. INTRODUCTION
 2. MATERIALS AND METHODS
 3. RESULTS
  3.1. Color Change after Heating with Ultrapure Water
  3.2. Color Change from Dye
  3.4. SEM, ED-XRF Analysis
  3.5. Analyze of Tensile Strength Measurement after Molding with PPS Resin and XPS
 4. DISCUSSION
 5. CONCLUSION
 6. ACKNOWLEDGEMENTS
 7. REFERENCES

키워드

magnesium alloy color change Lauric acid anodizing tensile strength

저자

  • Gu Min KANG [ Changwon Science High School, 159 beon-gil 30, Pyeongsan-ro, Uichang-gu, Changwon, Gyeongnam, Republic of Korea ] Corresponding author
  • Jin Sol KIM [ Changwon Science High School, 159 beon-gil 30, Pyeongsan-ro, Uichang-gu, Changwon, Gyeongnam, Republic of Korea ]
  • Jun Hyeok LIM [ Changwon Science High School, 159 beon-gil 30, Pyeongsan-ro, Uichang-gu, Changwon, Gyeongnam, Republic of Korea ]

참고문헌

자료제공 : 네이버학술정보

간행물 정보

발행기관

  • 발행기관명
    국제과학영재학회 [The Society for the International Gifted in Science]
  • 설립연도
    2006
  • 분야
    자연과학>자연과학일반
  • 소개
    과학영재를 위한 연구 활동을 통하여 과학영재를 발굴하고, 발굴된 과학영재가 과학 분야의 관련 연구 활동을 할 수 있도록 지원하여, 이들이 과학 관련 분야의 진로를 선택하도록 장려함으로써 국제경쟁력을 갖춘 우수 과학기술인을 배출하고 국가 경제발전 및 문화창달과 세계 과학 발전에 기여함을 목적으로 한다.

간행물

  • 간행물명
    APEC Youth Scientist Journal [APEC 청소년 과학학술지]
  • 간기
    반년간
  • pISSN
    2005-5625
  • 수록기간
    2009~2022
  • 십진분류
    KDC 405 DDC 505

이 권호 내 다른 논문 / APEC Youth Scientist Journal Vol. 7 No.1

    피인용수 : 0건 (자료제공 : 네이버학술정보)

    함께 이용한 논문 이 논문을 다운로드한 분들이 이용한 다른 논문입니다.

      출처 : 네이버학술정보

        0개의 논문이 장바구니에 담겼습니다.

        페이지 저장
        소속기관 조회
        이용자님의 소속기관(단체)이 서비스에 가입되어 있는지 확인해 보십시오.
        기관회원에 소속되어 있는 이용자는 원문을 무료로 이용할 수 있습니다.