Purpose: The objective of this study was to evaluate influence of mechanical properties of gingival shade composite resins(GSCRs) according to thermocycling treatment. Methods: The material utilized in this study was Crea.lign(CGR), Twiny flow(TGF) and Twiny(TGP). Total sixty specimens were fabricated with a dimension of 25×2×2mm according to the ISO 4049. After fabrications, specimens of before and after thermocycling(to 55℃ from 5℃) were stored in the distilled water for 24 hours at the 37℃. Three-point flexural test was performed in universal testing machine(Instron 5966, USA) at a crosshead speed of 1 mm/min. Flexural strength, flexural modulus and work of fracture according to the thermocycling were analyzed using a one-way ANOVA analysis. Surface analysis of GSCRs after thermocycling evaluated using the scanning electron microscope. Results: : The highest FS was measured in TGP group of NTC group and lowest in CGR group after TC. After TC, FS and FM decreased in CGR and TGP groups, but TGF increased. There was a statistically significant difference between FS and WOF in GSCRs(p <0.05). But FM did not show any significant difference after TC (p> 0.05).The strength of the characteristic exceeded the flexural strength required by ISO 4049(> 80 MPa). Weibull modulus(m) showed the highest reliability in the TGP group (m = 14.22), and the reliability of the TGF and TGP groups after TC decreased. Conclusion: Thermocycling treatment is important factor influence of mechanical properties with gingival shade composite resins. Therefore, we recommended that mechanical properties need to get useful information and accuracy for life-span expectancy according to the thermocycling treatment.

목차

[Abstract]
 Ⅰ. 서론
 Ⅱ. 연구 방법
  1.연구 대상
  2. 시편 제작
  3. 열 순환(thermocycling) 처리
  4. 굽힘 강도 측정
  5. 와이블(Weibull) 분석
 Ⅲ. 결과
 Ⅳ. 고찰
 Ⅴ. 결론
 REFERENCES

키워드

저자

• 임용운 [ Yong-Woon Im | 단국대학교 치과대학 생체재료학연구실 ]
• 황성식 [ Seong-Sig Hwang | 경동대학교 치기공학과 ] Corresponding author

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  대한치과기공학회지 [THE JOURNAL OF KOREAN ACADEMY OF DENTAL TECHNOLOGY]

• 간기

  계간

• pISSN

  1229-3954

• eISSN

  2288-5218

• 수록기간

  1979~2026

• 등재여부

  KCI 등재

• 십진분류

  KDC 515 DDC 617