Inorganic stiffening agents were prepared by mixing paper sludge incineration ash, blast furnace slag fine powder quicklime, anhydrous gypsum and fly ash. The main components of the solidifying agent developed for sludge treatment were SiO, Al2O3, TiO2, Fe2O3, Mn2O3, CaO, MgO, Na2O, K2O, P₂O, and SO3. Unlike cement, the developed solidifying agent did not contain Cr6+, which is known as a carcinogen. Heavy metals and oil contaminated soil were mixed with solidifying agent and cured for 7 days and the heavy metal content was below the environmental standard. Sewage sludge cake, food waste and solidifying agent were mixed with each other, and after 7 days curing, soil component test showed that the heavy metal content was below the environmental standard. After mixing the sludge, solidifying agent and additive mixture into the beaker, the ammonia concentration was measured to be 0 after 3 days.

한국어

제지슬러지 소각재, 용광로 슬래그 미세분말 생석회, 무수석고 및 프라이애쉬 등을 혼합하여 무기계고화 재를 제조하였다. 슬러지 처리용으로 개발된 고화재의 주성분은 SiO, Al₂O3, TiO2, Fe₂O3, Mn₂O3, CaO, MgO, Na₂O, K₂O, P₂O, SO₃이었다. 시멘트와 달리, 개발된 고화재에는 발암물질로 알려진 Cr6+가 함유되지 않았다. 중금속 및 기름 오염토를 고화재와 혼합한 후 7일간 양생하여 빗물용출실험을 시행한 결과 중금속이 미미하였다. 하수슬러지 케이크 및 음식물쓰레기와 고화재를 각각 혼합하여 7일 양생 후 토양성분실험을 한 결과 중금속 함량이 환경기준치 이하로 나타났다. 슬러지, 고화재 및 첨가제 혼합시료를 비이커에 혼합한 후 암모니아 농도를 측정한 결과 3일 후 0이 되었다.

목차

요약
 Abstract
 1. 서론
 2. 슬러지용 고화재 제조
 3. 성분검사
 4. 슬러지와 고화재 혼합실험
  4.1 중금속 유해성
  4.2 유기물 고정과 악취제거
 5. 결론
 REFERENCES

키워드

저자

• 한두희 [ Doo Hee Han | 중소기업기술융합연구소, 청운대학교 ] Corresponding author

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  한국융합학회논문지 [Journal of the Korea Convergence Society]

• 간기

  월간

• pISSN

  2233-4890

• 수록기간

  2010~2022

• 십진분류

  KDC 530 DDC 620