Fe(NO3)3 수용액의 농도와 침지시간에 따른 지르코니아의 색상 및 특성 변화
The change of color and physical properties of zirconia according to the variation of concentration and dipping time of Fe(NO3)3 solution

첫 페이지 보기
  • 발행기관
    대한치과기공학회 바로가기
  • 간행물
    대한치과기공학회지 KCI 등재후보 바로가기
  • 통권
    Vol.38 No.4 (2016.12)바로가기
  • 페이지
    pp.281-290
  • 저자
    서정일, 박원욱, 고재숙
  • 언어
    한국어(KOR)
  • URL
    https://www.earticle.net/Article/A298466

※ 기관로그인 시 무료 이용이 가능합니다.

4,000원

원문정보

초록

영어
Purpose:The increased aesthetic requirements and demands of patients have resulted in the developments of coloring liquid for zirconia. Methods: In this study, zirconia block was dipped into Fe(NO3)3solution, which showed a color and then concentration of Fe(NO3)3and zirconia's color and physical properties depending on the dipping time were observed and compared with exclusive coloring solutions. As the result, the following conclusions were obtained. Results: When compared with the specimens that were colored using exclusive solutions, L* value rose overall depending on the concentration of Fe(NO3)3and a* value was red in the form of (+) in all the specimens. Also, b* value was in the form of (+) at 0.5 to 1 ßfl, but was in the form of (-) at 1.5 to 2 ßfl. The dipping time did not highly influence L* value, but a* value and b* value were directly opposite to the specimens, which were not colored, except the sample that was dipped for only 2 seconds. When compared with exclusive coloring solutions, Fe(NO3)3had the most similar color at 0.5 to 1 ßfl and the longer the coloring time, the higher the rate of color change became. In relation to the density change depending on the addition of Fe(NO3)3, there was the lowest density at 2 ßfl and the density was increased in the specimens that were not colored. Conclusion: These results show that Fe(NO3)3solution can be used to make colored zirconia. It is expected that newly made colored zirconia can be used in clinical practice because the colored zirconia not only possesses the mechanical properties that all ceramic core material should have but also was biocompatible to a living cells.

목차

[Abstract]
 Ⅰ. 서론
 Ⅱ. 연구 방법
  1. 연구재료
  2. 시편제조
  3. 색상평가
  4. 밀도측정
  5. 미세구조관찰
  6. 비커스경도시험
 Ⅲ. 결과
  1. Fe(NO3)3수용액의농도에따른색상및물리적특성
  2. Fe(NO3)3수용액의침지시간에따른색상및물리적특성
  4. EDS 분석
 Ⅳ. 고찰
 Ⅴ. 결론
 REFERENCES

키워드

3Y-TZP zirconia Fe(NO3)3 solution Color order system

저자

  • 서정일 [ Jeong Il Seo | 진주보건대학교치기공과 ] 교신저자
  • 박원욱 [ Won Uk Park | 진주보건대학교치기공과 ]
  • 고재숙 [ Go Jae-Sook | 진주보건대학교치기공과 ]

참고문헌

자료제공 : 네이버학술정보

간행물 정보

발행기관

  • 발행기관명
    대한치과기공학회 [The Korean Academy Of Dental Technology]
  • 설립연도
    1979
  • 분야
    의약학>치의학
  • 소개
    본 학회는 치과기공에 관한 모든 분야의 연구와 회무를 총괄하기 위하여 세분화된 분과학회의 회원 상호간 학술교류와 정보를 수집하고, 보수교육 및 학술대회 준비, 진행과 학회지 발간등의 업무를 효율적으로 수행함을 목적으로 한다.

간행물

  • 간행물명
    대한치과기공학회지 [THE JOURNAL OF KOREAN ACADEMY OF DENTAL TECHNOLOGY]
  • 간기
    계간
  • pISSN
    1229-3954
  • eISSN
    2288-5218
  • 수록기간
    1979~2026
  • 등재여부
    KCI 등재
  • 십진분류
    KDC 515 DDC 617

이 권호 내 다른 논문 / 대한치과기공학회지 Vol.38 No.4

    피인용수 : 0건 (자료제공 : 네이버학술정보)

    함께 이용한 논문 이 논문을 다운로드한 분들이 이용한 다른 논문입니다.

      출처 : 네이버학술정보

        0개의 논문이 장바구니에 담겼습니다.

        페이지 저장
        소속기관 조회
        이용자님의 소속기관(단체)이 서비스에 가입되어 있는지 확인해 보십시오.
        기관회원에 소속되어 있는 이용자는 원문을 무료로 이용할 수 있습니다.