Purpose: It is to compare and evaluate the change of the wear rate and phase variation of the Zirconia before and after the sintering after the grinding by a high speed equipment manufactured for the Zirconia. Methods: The specimen of the sintered Zirconia was manufactured as size of 15㎜×15㎜×2㎜. The grinding has been applied to each of all pieces of each test groups for a minute fit for each condition at same speed of 50,000 rpm by a diamond bur at high speed handpiece with injection of the air and water. For the observation of the surface before and after the sintering of the each test piece, the cross section of it was observed as 100 magnification by a scanning electron microscope after it was coated by PT, and the diffraction analysis was performed by XDR to compare the crystal phase of the Zirconia. The average surface roughness value of all specimens were evaluated. The wear test was performed at room temperature by applying a load of 1kg for 120,000 cycles for the chewing period 6 months. Wear was analyzed for the enamel cusps by measurement of the vertical substance loss with a laser scanner. Conclusion: The phase variation from the tetragonal phase to the monoclinic phase was confirmed in the test group of the pre-sintered Zirconia after the grinding, and the value of the surface roughness and the wear rate was increased in experimental group.

목차

Abstract
 Ⅰ. 서론
 Ⅱ. 연구 방법
  1. 시편 제작
  2. 실험 방법 및 분석
  3. 통계 분석
 Ⅲ. 결과
 Ⅳ. 고찰
 Ⅴ. 결론
 REFERENCES

키워드

저자

• 김민정 [ Min-Jeong Kim | 경북대학교 의용생체공학과 ]
• 김임선 [ Im-Sun Kim | 대구보건대학교 치기공과 ] 교신저자
• 최병환 [ Byung-Hwan Choi | 대구보건대학교 치기공과 ]
• 김원기 [ Won-Gi Kim | 대구보건대학교 치기공과 ]

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  대한치과기공학회지 [THE JOURNAL OF KOREAN ACADEMY OF DENTAL TECHNOLOGY]

• 간기

  계간

• pISSN

  1229-3954

• eISSN

  2288-5218

• 수록기간

  1979~2026

• 등재여부

  KCI 등재

• 십진분류

  KDC 515 DDC 617