The aim of this study was to obtain information on the ancient material of cast bronze through an investigation of the microstructure and impurity characteristics of the casting. Three Koryo bronze coins were analyzed using an optical microscope, scanning electron microscope, and electron dispersive X-ray analyses were used to determine the composition of the specimens. The three coins had 4 phases: αphase, δphase, Pb, and impurities (Cu2S). Cu2S was found to exist near Pb or in δphase. Cu2S is the inter mediate product of copper ore refining. Therefore, the copper ore was not completely refined. To find out the characteristic of Cu2S, we melt 1)Koryo bronze coin and 2)Cu2S and Pb powder at 1273 K. The reaction between Cu2S and Pb at 1273 K yielded fine Cu and black gas, which was identified to be PbS and is presented below: Cu2S+Pb → PbS↑+2Cu.

한국어

청동으로 주조된 공예품의 금속 조직학적 연구를 통해 그 내부에 관찰되는 불순물을 추측하고, 그 물질의 특성을 파악하여 향후 제련 및 과거 청동 주물 제조 방법 및 재료 연구의 기초데이터를 제공하는 것을 목적으로 한다. 분석에는 SEM-EDS, XRD, 광학현미경을 이용하였다. 분석 결과, 3점의 시료는 α상, δ상, Pb, 불순물 입자인 Cu2S의 4개의 상으로 이루어져 있으며, Cu2S입자는 황동광을 제련하였을 때 생기는 제련 중간 발생물로 추측된다. 이 입자는 Pb와 인접하여 주로 관찰되며, δ상 내부에서 관찰되는 경우도 있었다. Cu2S의 입자 특성을 파악하기 위하여 1) 고려경 파편 및 2) Cu2S와 Pb을 1273 K에서 녹여 10℃/min의 속도로 냉각시켰다. 두 가지 실험으로 공통적으로 검은색 연기가 발생하였으며, 이 연기를 분석한 결과 PbS이었다. Cu2S와 Pb을 반응 시킨 실험에서는 Cu2S+Pb → PbS↑+2Cu의 반응식을 얻었다.

목차

초록
 ABSTRACT
 1. 서론
 2. 연구방법
  2.1. 금속조직학적 분석
  2.2. 불순물 특성 파악 실험
 3. 연구 결과
  3.1. 동전의 외관 관찰 및 조성분석 결과
  3.2. 금속조직 관찰 결과
  3.3. 불순물 입자의 분석 결과
  3.4. 재주조 실험을 통한 Cu2S 입자 연구
  3.5. Cu2S 입자 거동 원인 연구
 4. 결론
 REFERENCES

키워드

저자

• 최정은 [ Jung Eun Choi | 대통령기록관 보존복원과 ] Corresponding author

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  보존과학회지 [Journal of Conservation Science]

• 간기

  연5회

• pISSN

  1225-5459

• eISSN

  2287-9781

• 수록기간

  2003~2026

• 등재여부

  KCI 등재

• 십진분류

  KDC 602 DDC 700