In this paper, we have studied a sheet resistance property of N- and P-type thin films deposited on ITO glass by use of RF magnetron sputtering. The N-type samples which has the deposition condition of 150W RF power, shows the highest current value, and the samples deposited for 15 minutes shows a better Ohmic contact property. As the substrate temperature, RF power and deposition time are increased, the sheet resistance of the samples is increased, and the low sheet resistance sample shows a better I-V property. The P-type samples shows the highest current value by 150W RF power condition as similar as N-type samples. and the samples deposited for 20 minutes shows a better ohmic contact property. The sheet resistance of the both types samples is increased as increasing RF power and deposition time.

한국어

본 연구는 RF 마그네트론 스퍼터링을 이용하여 ITO glass 위에 N-Type과 P-Type 박막을 증착하여 증착 조건에 따른 면저항 특성을 확인하였다. N-Type의 I-V특성은 RF Power가 150 W 일 때 전류의 값이 가장 높은 것으로 나타났고, 15분을 증착하였을 때 기울기가 일정하게 나타나면서 Ohmic contact이 잘 이루어지는 것을 확인 할 수 있었다. 기판온도와 RF Power 및 증착시간이 증가함에 따라 면저항이 증가하는 것으로 나타났고, 면저항이 작은 값일수록 I-V 특성이 잘 나타났다. P-Type 에서도 N-Type과 비슷한 양상을 보이는데, RF Power가 150 W일때 전류가 가장 높은 것으로 나타났고, 20분을 증착하였을 때 Ohmic contact이 잘 이루어지는 것을 확인 할 수 있었다. 면저항 또한 N-Type과 비슷하게 RF Power와 증착시간이 증가함에 따라 면저항이 증가하는 것을 확인 할 수 있었다.

목차

요약
 Abstract
 1. 서론
 2. 실험방법
 3. 결과 및 고찰
 4. 결론
 References

키워드

저자

• 박정철 [ Jung-Cheul Park | 정회원, 가천대학교 전자공학과 ]
• 추순남 [ Soon-Nam Chu | 정회원, 가천대학교 전자공학과 ] 교신저자

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  한국인터넷방송통신학회 논문지 [The Journal of the Institute of Internet, Broadcasting and Communication]

• 간기

  격월간

• pISSN

  2289-0238

• eISSN

  2289-0246

• 수록기간

  2001~2025

• 십진분류

  KDC 326 DDC 380