A commercially available copper mesh was investigated as an iodine off-gas capturing medium for pyroprocessing, with an aim to replace costly silver based adsorbents. Theoretical calculation results suggested that the reaction between metallic copper and gaseous iodine will occur spontaneously to produce copper iodide in the temperature range of 100 ~ 500℃. The effect of the reaction temperature on iodine capturing efficiency was investigated by experimentation, and it was found that 5 and 6 wt% of iodine (initial mass 2.0 g) was captured by a single copper mesh (0.26 g) at 300 and 400℃, respectively. The repeated experimental results also suggested that copper utilization can be increased with the help of the spontaneous detachment of the reaction product (CuI) from a copper mesh. The formation of the CuI phase was confirmed using the X-ray diffraction technique, and the surface morphology of the reaction product was observed using scanning electron microscopy.

한국어

본 연구에서는 파이로프로세싱에서 발생하는 배기체 내 요오드 포집을 위한 매질로서 고가의 은 기반 흡착제를 대체하기 위 한 상용 구리메쉬의 가능성에 대해 연구하였다. 열역학적 계산을 통해 구리 금속과 요오드 기체의 반응은 100 ~ 500℃ 온도 범위에서 자발적으로 일어나며 요오드화구리(CuI)를 형성할 것으로 예상되었다. 실험을 통해 반응 온도에 따른 요오드 포 집 효율의 영향을 분석한 결과, 1개의 구리메쉬(질량 0.26 g)를 이용하여 반응 온도를 300, 400℃로 변화하였을 때 각각 5 및 6 wt%의 요오드(초기질량 2.0 g)가 포집됨을 확인하였다. 또한, 반복 실험 결과를 토대로 구리메쉬 표면에 형성된 반응 생성 물(CuI)의 자발적인 탈리 현상으로 구리의 활용률이 증가할 수 있음을 확인하였다. 반응 생성물의 CuI 상 형성은 X-선 회절 실험을 통해 확인하였으며, 표면 분석은 주사전자현미경을 이용하여 수행하여 그 결과를 보고하였다.

목차

Abstract
 요약
 1. Introduction
 2. Experimental
 3. Results and Discussion
  3.1 Theoretical calculations
  3.2 Experimental results
 4. Conclusions
 Acknowledgements
 References

키워드

저자

• Min Ku Jeon [ 전민구 | Korea Atomic Energy Research Institute, University of Science and Technology ] Corresponding Author
• Tae Kyo Lee [ 이태교 | Korea Atomic Energy Research Institute ]
• Yong Taek Choi [ 최용택 | Korea Atomic Energy Research Institute ]
• Hee-Chul Eun [ 은희철 | Korea Atomic Energy Research Institute, University of Science and Technology ]
• Jung Hoon Choi [ 최정훈 | Korea Atomic Energy Research Institute ]
• Hwan-Seo Park [ 박환서 | Korea Atomic Energy Research Institute, University of Science and Technology ]
• Jin-Mok Hur [ 허진목 | Korea Atomic Energy Research Institute ]
• Do-Hee Ahn [ 안도희 | Korea Atomic Energy Research Institute, University of Science and Technology ]

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  방사성폐기물학회지 [Journal of Nuclear Fuel Cycle and Waste Technology (JNFCWT)]

• 간기

  계간

• pISSN

  1738-1894

• 수록기간

  2003~2017

• 십진분류

  KDC 559 DDC 629