In order to develop 2nd generation (2G) high-temperature superconducting (HTS) wires as commercial products, it is necessary to perform a high speed investigation of their superconducting performance. Room-temperature and non -contact optical scanning tools are necessary to verify the microstructure of the superconducting materials, the current flow below the critical temperature, and the critical current density. In this paper, we report our results of an inspection of the electrical transport properties of coated conductors. The samples that we used in our study were highly qualified rare-earth based coated conductors produced via co-evaporation, and SmBa2Cu3O7-y (SmBCO) was the superconducting materials used in our studies. A film grown on IBAD-MgO templates shows larger than 400 A/cm at 77 K and a self-field. The local transport properties of the films were investigated by room-temperature imaging by thermal heating. The room-temperature images show structural inhomogeneities on the surface of the films. Bolometric response imaging via low-temperature bolometric microscopy was used to construct the local current mapping at the surface. These results indicate that the non-uniform regions on the surface disturb the current flow, and laser scanning images at room-temperature and at a low-temperature suggest a correlation between the structural properties and transport properties. Thus this method can be effective to evaluate the quality of the coated conductors.

목차

Abstract
 1. INTRODUCTION
 2. MEASUREMENT SYSTEM
 3. EXPERIMENTS
 4. RESULTS AND DISCUSSION
 5. CONCLUSION
 ACKNOWLEDGMENT
 REFERENCES

키워드

저자

• Gracia Kim [ Department of Physics, Ewha Womans University, Seoul, Korea ]
• Hye-Jin Jin [ Department of Physics, Ewha Womans University, Seoul, Korea ]
• William Jo [ Department of Physics, Ewha Womans University, Seoul, Korea ] Corresponding author

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  한국초전도·저온논문지 (구 한국초전도저온공학회논문지) [Progress in Superconductivity and Cryogenics]

• 간기

  계간

• pISSN

  1229-3008

• eISSN

  2287-6251

• 수록기간

  1999~2026

• 등재여부

  KCI 등재,SCOPUS

• 십진분류

  KDC 427 DDC 537