Friction Stir Welding (FSW) has been applied to AA5754-H111 alloy. An in-depth analysis of the influence of the process parameters has been performed using Taguchi method. Through the optimization of the process parameters it has been observed what the best process conditions for the different mechanical properties. It was observed that for tensile properties the best that lower advancing speeds and lower applied forces would be more beneficial to obtain a better tensile behavior. On the other hand, the higher advancing speeds and higher applied forces have proven to give a better bending behavior. The optimization algorithm has proven to be efficient giving welded samples with 98% efficiency, very close to the base material behavior. The corrosion testing has proven that these alloys are very resistant to corrosion although some caution should be taken regarding the “root defect”.

목차

Abstract
 1. Introduction
 2. Experimental Procedure
 3. Results
 4. Discussion of Results and Conclusions
 Acknowledgements
 References

키워드

저자

• F. Nascimento [ Faculdade de Engenharia at Universidade do Porto, Porto, Portugal ]
• P. Vilaça [ Department of Engineering Design and Production, School of Engineering, Aalto University, Finland ]
• R. Miranda [ FCT-UNL, Faculty of Science and Technology, Universidade Nova de Lisboa, Monte da Caparica, Portugal ]
• J. C. S. Fernandes [ DEQ / ICEMS, Instituto Superior Técnico, Universidade Técnica de Lisboa, Lisboa, Portugal ]
• F. M. Andrade Pires [ Faculdade de Engenharia at Universidade do Porto, Porto, Portugal ]

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  International Journal of Hybrid Information Technology

• 간기

  격월간

• pISSN

  1738-9968

• 수록기간

  2008~2016

• 십진분류

  KDC 505 DDC 605