A comparative study on the flux pinning properties of Zr-doped YBCO film with those of Sn-doped one prepared by metal-organic deposition

첫 페이지 보기
  • 발행기관
    한국초전도저온학회 (구 한국초전도저온공학회) 바로가기
  • 간행물
    한국초전도·저온논문지 (구 한국초전도저온공학회논문지) KCI 등재 바로가기
  • 통권
    Vol.15 No.4 (2013.12)바로가기
  • 페이지
    pp.15-20
  • 저자
    S. M. Choi, G. M. Shin, Y. S. Joo, S. I. Yoo
  • 언어
    영어(ENG)
  • URL
    https://www.earticle.net/Article/A212565

※ 기관로그인 시 무료 이용이 가능합니다.

4,000원

원문정보

초록

영어
We investigated the flux pinning properties of both 10 mol% Zr-and Sn-doped YBa2Cu3O7-δ (YBCO) films with the same thickness of ~350 nm for a comparative purpose. The films were prepared on the SrTiO3 (STO) single crystal substrate by the metal-organic deposition (MOD) process. Compared with Sn-doped YBCO film, Zr-doped one exhibited a significant enhancement in the critical current density (Jc) and pinning force density (Fp). The anisotropic Jc,min/Jc,max ratio in the field-angle dependence of Jc at 77 K for 1 T was also improved from 0.23 for Sn-doped YBCO to 0.39 for Zr-doped YBCO. Thus, the highest magnetic Jc values of 9.0 and 2.9 MA/cm2 with the maximum Fp (Fp,max) values of 19 and 5 GN/m3 at 65 and 77 K for H // c, respectively, could be achieved from Zr-doped YBCO film. The stronger pinning effect in Zr-doped YBCO film is attributable to smaller BaZrO3 (BZO) nanoparticles (the average size ≈ 28.4 nm) than YBa2SnO5.5 (YBSO) nanoparticles (the average size ≈ 45.0 nm) incorporated in Sn-doped YBCO film since smaller nanoparticles can generate more defects acting as effective flux pinning sites due to larger incoherent interfacial area for the same doping concentration.

목차

Abstract
 1. INTRODUCTION
 2. EXPERIMENTAL PROCEDURE
 3. RESULTS AND DISCUSSION
 4. CONCLUSION
 ACKNOWLEDGMENT
 REFERENCES

키워드

Metal-organic deposition YBCO film YBa2SnO5.5 and BaZrO3 nanoparticles Flux pinning

저자

  • S. M. Choi [ Department of Materials Science and Engineering, Research Institute of Advanced Materials (RIAM), Seoul National University, Seoul, Korea ]
  • G. M. Shin [ Department of Materials Science and Engineering, Research Institute of Advanced Materials (RIAM), Seoul National University, Seoul, Korea ]
  • Y. S. Joo [ Department of Materials Science and Engineering, Research Institute of Advanced Materials (RIAM), Seoul National University, Seoul, Korea ]
  • S. I. Yoo [ Department of Materials Science and Engineering, Research Institute of Advanced Materials (RIAM), Seoul National University, Seoul, Korea ] Corresponding author

참고문헌

자료제공 : 네이버학술정보

간행물 정보

발행기관

  • 발행기관명
    한국초전도저온학회 (구 한국초전도저온공학회) [The Korean Society of Superconductivity and Cryogenics (KSSC)]
  • 설립연도
    1998
  • 분야
    공학>전기공학
  • 소개
    21세기 핵심기술인 초전도공학과 저온공학분야의 기술 수준을 향상시키고, 선진 외국의 관련 학회와의 국제 교류 뿐만 아니라 이 분야에서 산.학.연의 학술활동 및 기술교류의 구심점으로의 그 역할을 성실히 수행하고자 한다.

간행물

  • 간행물명
    한국초전도·저온논문지 (구 한국초전도저온공학회논문지) [Progress in Superconductivity and Cryogenics]
  • 간기
    계간
  • pISSN
    1229-3008
  • eISSN
    2287-6251
  • 수록기간
    1999~2026
  • 등재여부
    KCI 등재,SCOPUS
  • 십진분류
    KDC 427 DDC 537

이 권호 내 다른 논문 / 한국초전도·저온논문지 (구 한국초전도저온공학회논문지) Vol.15 No.4

    피인용수 : 0건 (자료제공 : 네이버학술정보)

    함께 이용한 논문 이 논문을 다운로드한 분들이 이용한 다른 논문입니다.

      출처 : 네이버학술정보

        0개의 논문이 장바구니에 담겼습니다.

        페이지 저장
        소속기관 조회
        이용자님의 소속기관(단체)이 서비스에 가입되어 있는지 확인해 보십시오.
        기관회원에 소속되어 있는 이용자는 원문을 무료로 이용할 수 있습니다.