Silicon nanowires were detached and obtained from silicon nanowire arrays on silicon substrate using a ultrasonomethod. Silicon nanowire arrays on silicon substrate were prepared with an electroless metal assisted etching of p -type silicon. The etching solution was an aqueous HF solution containing silver nitrate. SEM observation shows that wellaligned nanowire arrays perpendicular to the surface of the silicon substrate were produced. After sonication of silicon nanowire array, an individual silicon nanowire was confirmed by FESEM. Optical characteristics of SiNWs were measured by FT-IR spectroscopy. The surface of SiNWs are terminated with hydrogen.

목차

Abstract
 1. Introduction
 2. Experimental Section
  2.1. Preparation of Silicon Nanowires
  2.2. Instrumentation and Data Acquisition
 3. Results and Discussion
 4. Conclusion
 Acknowledgment
 References

키워드

저자

• Sung-Gi Lee, [ Sung-Gi Lee | Department of Chemistry, Chosun University, Gwangju 501-759, Korea ]
• Donghee Sihn [ Department of Chemistry, Chosun University, Gwangju 501-759, Korea ]
• Sungyong Um [ Department of Chemistry, Chosun University, Gwangju 501-759, Korea ]
• Bomin Cho [ Department of Chemistry, Chosun University, Gwangju 501-759, Korea ]
• Sungryong Kim [ Department of Chemistry, Chosun University, Gwangju 501-759, Korea ]
• Honglae Sohn [ Department of Chemistry, Chosun University, Gwangju 501-759, Korea ] Corresponding author

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  통합자연과학논문집(구 조선자연과학논문집) [Journal of Integrative Natural Science]

• 간기

  계간

• pISSN

  2005-1042

• 수록기간

  2008~2025

• 등재여부

  KCI 등재

• 십진분류

  KDC 405 DDC 505