지르코니아와 포세린의 전단결합강도
Shear Bond Strength Between Zirconia and Porcelain
-
- 발행기관
- 대한치과기공학회 바로가기
-
- 간행물
- 대한치과기공학회지 KCI 등재후보 바로가기
-
- 통권
- Vol.33 No.1 (2011.03)바로가기
-
- 페이지
- pp.1-6
-
- 저자
-
- 언어
- 한국어(KOR)
-
- URL
- https://www.earticle.net/Article/A152992
※ 기관로그인 시 무료 이용이 가능합니다.
4,000원
원문정보
초록
- 영어
- Purpose: To examine the shear bond strengths of zirconia and veneering ceramic according to their surface processing.
Methods: The test samples were divided into three groups: one without zirconia surface processing, one sandblasted, and one sandblasted then 3% etched. Then veneering ceramic was fired on all test samples, and their
shear bond strengths were measured.
Results: The test samples of the control group (Z1) showed the lowest shear bond strengths of 21.82±1.02 MPa.
The shear bond strengths of Z2 and Z3 (28.25±0.72 and 26.23±0.82 MPa, respectively) were relatively higher than those of the control group. The fracture surface of the control group showed adhesive fractures while the test groups had relatively large numbers of cohesive fractures.
Conclusion: The shear bond strength was high in the test groups with surface processing while the fracture surfaces showed compound fractures of adhesive and cohesive fractures.
목차
[Abstract]
Ⅰ. 서론
Ⅱ. 연구 방법
1. 연구재료 및 시편제조
2. 기기분석
Ⅲ. 결과
1. 전단결합강도의 측정
2. 주사전자현미경(SEM) 관찰
Ⅳ. 고찰
Ⅴ. 결론
참고문헌
키워드
shear bond strengths zirconia저자
간행물 정보
발행기관
-
- 발행기관명
- 대한치과기공학회 [The Korean Academy Of Dental Technology]
- 설립연도
- 1979
- 분야
- 의약학>치의학
- 소개
- 본 학회는 치과기공에 관한 모든 분야의 연구와 회무를 총괄하기 위하여 세분화된 분과학회의 회원 상호간 학술교류와 정보를 수집하고, 보수교육 및 학술대회 준비, 진행과 학회지 발간등의 업무를 효율적으로 수행함을 목적으로 한다.
간행물
-
- 간행물명
- 대한치과기공학회지 [THE JOURNAL OF KOREAN ACADEMY OF DENTAL TECHNOLOGY]
- 간기
- 계간
- pISSN
- 1229-3954
- eISSN
- 2288-5218
- 수록기간
- 1979~2026
- 등재여부
- KCI 등재
- 십진분류
- KDC 515 DDC 617
이 권호 내 다른 논문 / 대한치과기공학회지 Vol.33 No.1
피인용수 : 0건 (자료제공 : 네이버학술정보)
함께 이용한 논문 이 논문을 다운로드한 분들이 이용한 다른 논문입니다.
출처 : 네이버학술정보
0개의 논문이 장바구니에 담겼습니다.