Purpose: The purpose of this study was to evaluate the fracture strength between the core and veneering ceramic according to 2 core materials, In-Ceram Alumina and In-Ceram Zirconia, fabricated by electro ceramic layering technique. 2 different fixed partial denture cores of three units were veneered by veneering ceramic(Ceranion, Noritake) (n=10).
Methods: The fracture strengths between the core and veneering ceramic were measured through the 3 point bending test. The interfaces between the core and veneering ceramic were observed with the X-ray dot mapping of EPMA.
Results: The result of fracture strength was observed that IZP group, In-Ceram Zirconia core, had higher fracture strength. IPA group, In-Ceram Alumina core, had fracture strength of 359.9( 86.2) N. IZP group, In-Ceram Zirconia core, had fracture strength of 823.2( 243.0) N. X-ray dot mapping observation showed that a major element in the core and veneering ceramic of IPA group was alumina and silica, respectively. No binder was observed in interfaces between the core and veneering ceramic, and no ion diffusion or transition was observed between the core and veneering ceramic. However, apparent ion diffusion or transition was observed between the core and veneering ceramic of IZP group.
Conclusion: Therefore, IZP group was evaluated to have the excellent mechanical property.

목차

[Abstract]
 Ⅰ. 서론
 Ⅱ. 실험 방법
  1. 실험 재료
  2. 실험 방법
 Ⅲ. 실험 결과
  1. 굵고 피절 강도
  2. 계면 관찰
 Ⅳ. 실험 고찰
 Ⅴ. 결론
 참고문헌

키워드

저자

• 정인성 [ In-Sung Chung | 부산가톨릭대학교 보건과학대학 치기공학과 ]
• 김치영 [ Chi-Young Kim | 부산가톨릭대학교 보건과학대학 치기공학과 ] 교신저자

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  대한치과기공학회지 [THE JOURNAL OF KOREAN ACADEMY OF DENTAL TECHNOLOGY]

• 간기

  계간

• pISSN

  1229-3954

• eISSN

  2288-5218

• 수록기간

  1979~2026

• 등재여부

  KCI 등재

• 십진분류

  KDC 515 DDC 617