The purpose of this study is to investigate the sulfate attack resistance of concrete containing copper slag. The specimens were made with copper slag as various replacement ratio(10, 20, 30%), plain concrete and concrete containing blast-furnace slag, silica fume. and with W/B ratio fixed 0.45. In order to figure out the resistance of sulfate attack, specimens were immerged in the 10% magnesium sulfate solution for 91 days, Compressive strength, S.D.F(Sulfate Deterioration Factor), weight change and SEM(Scanning Electron Microscope) were tested. From the test results, blast furnace slag replacement ratio of 30% was the best for sulfate attack resistance. Also, copper slag replacement ratio up to 20% increased sulfate attack resistance, but copper slag replacement ratio of 30% concrete was a tendency to decrease drastically. However, the severe deterioration due to sulfate attack was found in silica fume replacement ratio of 15% concrete.

한국어

본 연구의 목적은 동제련 슬래그를 혼입한 콘크리트의 황산염침식 저항성을 연구하는데 있다. 동제련 슬래그를 10, 20, 30% 혼입한 콘크리트와 플레인 콘크리트, 고로슬래그, 실리카흄을 혼입한 콘크리트를 제작하였고, 물-결합재비는 45%로 고정하였다. 황산염 저항성 실험을 위해 10%의 황산마그네슘 용액에 재령 84일 간 침지하여 실험하였고, 압축강도, 황산염 성능저하지수, 질량변화율과 SEM촬영 등을 실험하였다. 실험결과에 따르면, 고로슬래그를 30% 치환한 콘크리트가 가장 우수한 황산염침식 저항성을 나타내었다. 또한, 동제련 슬래그의 치환율이 20%까지는 저항성이 증가하였으나, 치환율이 30%일 경우 급격히 감소하는 경향을 나타내었다. 그러나, 실리카흄을 15%혼입한 콘크리트가 황산염침식에 대해 가장 심각한 성능저하를 나타내었다.

목차

Abstract
 1. 서론
  1.1 연구배경 및 목적
 2. 실험계획 및 방법
  2.1 실험계획
  2.2 사용재료
  2.3 실험방법
 3. 실험결과 및 고찰
  3.1 굳지않은 콘크리트의 물리적 특성
  3.2 콘크리트의 압축강도
  3.3 황산염침식 저항성
 4. 결론
 참고문헌

키워드

저자

• 김영수 [ Kim, Young-Su | 부산대학교 건축학부, 교수 ]
• 양창진 [ Yang, Chang-Jin | 동서대학교 건축토목공학부, 교수 ] 교신저자

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  대한건축학회연합논문집 [Journal of the Regional Association of Architectural Institute of Korea]

• 간기

  격월간

• pISSN

  1229-5752

• 수록기간

  1999~2026

• 등재여부

  KCI 등재

• 십진분류

  KDC 540 DDC 690