Hyaluronic acid is good bio-compatibility material for soft tissue augmentation. But it is short
persistence with dissolved by enzyme in body. Currently, some researcher have studied for long
term persistence in body with cross linked hyaluronic acid for improve the this problem. We are
produced hyaluronic acid hydrogel by hyaluronic acid micro bead obtained from hyaluronic water
solution disperse in crosslinking agent and alcohol solution after cross linked for long term
persistence in body. This study is measure of residual volume at 4, 8, 12 week after implanted
hydrogel in NZW rabbit for evaluation of hyaluronic acid hydrogel durational properties in body.
As a result, be observed mostly persist and little decrease residual volume at 12th week
compared with at 4th week.

한국어

연조직 수복을 위해 이식되는 히알루론산은 생체적합성이 매우 우수하지만 체내 존재하는 효소에 의해 수일내로 분해 되는 단점이 있다. 이를 개선하기 위하여 가교를 통해 제조하는 수화겔의 연구가 많이 이루어지고 있다. 본 연구에서는 체내에서 단기간에 분해 되지 않는 수화겔 제조를 목적으로 히알루론산 수용액을 일정한 속도로 냉각관을 통과시켜 미세방울을 얻은 후 가교제에 침지하는 방법으로 가교된 히알루론산 수화겔을 제조하였다. 이렇게 제조된 히알루론산 수화겔의 체내 지속성을 평가하기 위하여 토끼 피부연조직에 이식한 후 3개월간 4주, 8주, 12주에서 이식된 수화겔의 잔류부피를 측정하였다. 그 결과 초기 이식된 수화겔의 부피에서 큰 변화 없이 대부분이 잔류하는 것이 관찰되었다.

목차

요약
 Abstract
 Ⅰ. 서론
 Ⅱ. 재료 및 방법
  2.1 재료
  2.2 조직 내 잔류시험
 Ⅲ. 결과 및 고찰
 Ⅴ. 참고문헌

키워드

저자

• 김진태 [ Jin Tae Kim | 충북대학교 신소재공학과 ]
• 최재하 [ Jae Ha Choi | 충북대학교 신소재공학과 ]

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  특허학연구 : 한국특허학회지 [JOURNAL OF KOREA INTELLECTUAL PATENT SOCIETY]

• 간기

  연간

• pISSN

  1598-8600

• 수록기간

  1999~2016

• 십진분류

  KDC 502 DDC 602