Poly (4-vinyipyridine-co-styrene) membrane containing Pyridine as fixed carrier was synthesized and characterized. And the active transport mechanism of Cl- and CCI3COO- with changing concentration of H+ and OH- was investigated. CCI3COO- was transported not only by a symport mechanism with transfer but also by an antiport mechanism with transfer, while CI- was transported only by a symport mechanism with transfer. Observing the initial flux of anions, salt formation constant between ions and membrane (K), and diffusion coefficient in membrane (D) were calculated as follows: for $C1-, K=4.60x102 mol-1cm3, D=1.57x10-3cm2/h$ and for CCI3COO-, K=1.10x104 mol-1cm3, D=1.14x10-34cm2/h.

한국어

본 연구에서는 고정전달자를 갖는 poly(4-vinylpyridine-co-styrene) 고분자막을 합성하여 이를 특성화하고, CI- 및 CCI3COO 의 H+ 및 OH- 농도차에 따른 능동전달 기구에 대하여 고찰하였다. 시험 범위 내에서 CI-의 능동전달은 주로 농도차를 구동력으로 한 병류수송(symprot)이 주가 되었으며 반면에 CCI3COO의 능동전달은 OH-의 농도차에 의한 향류 수성(antiport)의 영향이 큼을 알 수 있었다. 농도와 농도에 의한 음이온의 초기플럭스를 관찰함으로서, 고정전달자와 이온간의 엄형성계수, K와 이온의 막내 확산계수, D는 CI-의 경우 각각 4.60x102 mo-1cm3 및 1.57x103cm2/h, CCI3COO- 의 경우 각각 1.10x104 mol-1cm3 및 1.44x104cm2/h 이었다.

목차

ABSTRACT
 서론
 재료 및 방법
  막합성 및 특성화
  능동전달 실험
 결과 및 고찰
  막의 특성
  CI의 능동전달
  CCI3COO의 능동전달
 요약
 사용기호
 감사
 참고문헌

저자

• 이용현 [ Yong-Hyun Lee | 연세대학교 공과대학 화학공학과 ]
• 한정우 [ Jeong-Woo Han | 연세대학교 공과대학 화학공학과 ]
• 박돈희 [ Don-Hee Park | 전남대학교 공과대학 화학공학과 ]
• 조영일 [ Yung-II Jo | 연세대학교 공과대학 화학공학과 ]

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  KSBB Journal

• 간기

  격월간

• pISSN

  1225-7117

• 수록기간

  2009~2013

• 십진분류

  KDC 476 DDC 576