Tar is often produced during the carbonization of cellulose that limits the formation fibrous structure of the carbonized sample. This problem was reduced by applying a high temperature (up to 800℃) during carbonization process. Alternatively, dry cellulose was immerged in toluene and ultrasonicated prior to carbonization. In both cases, complete fibrous structures were not achieved. The formation of tar was reduced by the heat treatment of cellulose in the presence of HCl vapor before carbonization process. Such treatment before carbonization yielded mostly the fibrous structures of the carbonized sample as evident from SEM analysis. Similar results were found when the cellulose was subjected to a heat treatment in an inert condition followed by the removal of tar by the oxidation process prior to the carbonization.

한국어

셀룰로오스의 탄화과정에서는 셀룰로오스의 pyrolysis에 의해 생산된 타르에 의해 탄화 후, 셀룰로오스 탄화물의 섬유구조를 저해시키는 문제점이 존재한다. 이와 같은 결과는 800℃ 이상의 탄화온도와 건조 셀룰로오스를 toluene에 침지하고 초음파 처리 후 탄화한 탄화물에서 감소되지만, 섬유구조만의 탄화물을 얻을 수 없었다. 그러나 셀룰로오스의 탄화에서 타르의 생산을 감소시키는 HCl vapor flow 조건에서의 열처리 과정의 적용과 탄화과정 중 생성된 타르의 제거를 통해서 탄화 후, 대부분의 영역에서 섬유 구조를 갖는 탄화물을 얻을 수 있었다.

목차

Abstract
 서론
 재료 및 방법
  사용균주 및 균주 배양배지
  셀룰로오스 배양
  탄화
 결과 및 고찰
  셀룰로오스의 생산성
  탄화
 요약
 REFERENCES

키워드

저자

• 김봉균 [ Bong Gyun Kim | 선문대학교 생체분자재설계연구소 ]
• 송재경 [ Jae Kyung Sohng | 선문대학교 생체분자재설계연구소 ]
• 류광경 [ Kwangkyoung Liou | 선문대학교 생체분자재설계연구소 ]
• 이희찬 [ Hei Chan Lee | 선문대학교 생체분자재설계연구소 ] Corresponding author

참고문헌

발행기관

간행물

표지보기 관심저널 등록

• 간행물명

  KSBB Journal

• 간기

  격월간

• pISSN

  1225-7117

• 수록기간

  2009~2013

• 십진분류

  KDC 476 DDC 576